Cracking Behavior of Irradiated Ex-Plant Materials

Abstract

The cracking behavior of reactor core internal materials is a key factor for the long-term safety and availability of light water reactors. Subject to high-temperature coolant, thermal and mechanical loading, and neutron irradiation, reactor core internal materials are susceptible to several degradation mechanisms during power operation. To understand the long-term effects of neutron irradiation, irradiated materials harvested from a decommissioned reactor were studied for their cracking susceptibility and fracture resistance. Small compact-tension specimens were machined from different locations on the baffle plates with irradiation doses ranging from 0.06 to 48.5 dpa. Crack growth rate and fracture toughness J-resistance (J-R) curve tests were performed on these specimens in a simulated light water reactor environment, and the fracture morphologies of the tested samples were examined with a scanning electron microscope. All samples behaved similarly under cyclic loading, and no deteriorated corrosion-fatigue behavior was observed in the test environments. Under constant load, no elevated cracking susceptibility was observed either in these samples at low stress intensity factors. However, a rapid cracking behavior featuring very high crack growth rates was observed in several high-dose samples. This rapid crack growth behavior was activated when the applied stress intensity factor, K, was sufficiently high. Once activated, the rapid crack growth remained steady even when the K was lowered to the pre-activation level and stopped only when the K was reduced drastically. Yet, the rapid crack growth could be re-activated repeatedly in these samples by raising the K above the initial activation level. This rapid cracking response may be related to the severe irradiation embrittlement experienced by these samples. The J-R curve tests performed with these samples showed a significant decline in fracture toughness with increasing neutron irradiation. Local cracking at the crack tip facilitated by the severe irradiation embrittlement of this material may be responsible for the rapid crack growth behavior demonstrated by this decommissioned material.