Quantifying Thermal Output of Energetic Materials (LDRD Final Report)

Abstract

We present the results of an LDRD project, funded by the Nuclear Deterrence IA, to develop capabilities for quantitative assessment of pyrotechnic thermal output. The thermal battery igniter is used as an exemplar system. Experimental methodologies for thermal output evaluation are demonstrated here, which can help designers and engineers better specify pyrotechnic components , provide thermal output guidelines for new formulations, and generate new metrics for assessing component performance and margin given a known failure condition. A heat-transfer analysis confirms that the dominant mode of energy transfer from the pyrotechnic output plume to the heat pellet is conduction via deposition of hot titanium particles. A simple lumped-parameter model of titanium particle heat transfer and a detailed multi-phase model of deposition heat transfer are discussed. Pyrotechnic function, as defined by "go/no-go" standoff testing of a heat pellet, is correlated with experimentally measured igniter plume temperature, titanium metal particle temperature, and energy deposition. Three high-speed thermal diagnostics were developed for this task. A three-color imaging pyrometer, acquiring 100k images per second on three color channels, is deployed for measurement of titanium particle temperatures. Complimentary measurements of the overall igniter plume emission ("color") temperature were conducted using a transmission-grating spectrograph in line-imaging mode. Heat flux and energy deposition to a cold wall at the heat-pellet location were estimated using an eroding thermocouple probe, with a frequency response of ~5 kHz. Ultimate "go/no-go" function in the igniter/heat-pellet system was correlated with quantitative thermal metrics, in particular surface energy deposition and plume color temperature. Titanium metal-particle and plume color temperatures both experience an upper bound approximated by the 3245-K boiling point of TiO 2 . Average metal-particle temperatures remained nearly constant for all standoff distances at T = 2850 K, ± 300 K, while plume color temperature and heat flux decay with standoff—suggesting that heat-pellet failure results from a drop in metal-particle flux and not particle temperature. At 50% likelihood of heat-pellet failure, peak time-resolved plume color temperatures drop well below TiO 2 boiling to ~2000 - 2200 K, near the TiO 2 melting point. Estimates of peak heat flux decline from up to 1 GW/m 2 for near-field standoffs to below 320 MW/m 2 at 50% failure likelihood.