Preprocessing of municipal solid waste towards thermal insulating material

Abstract

Municipal solid waste (MSW) is one of the significant challenges in today’s world. A continuous surge in population, increasing living standards, and rapid urbanization are generating an enormous quantity of MSW. For example, the Environmental Protection Agency (EPA) reported that the total generation of MSW in the United States in 2018 was 292.4 million tons. Improper management of this MSW often leads to the release of greenhouse gases, emission of particulate matters, and formation of dioxins, which all ultimately contributes to climate change. Recycling these wastes via landfills with gas recovery and/or energy and material production via thermal and chemical conversions could be viable options to manage these challenges. Depending on the inherent chemical and structural properties of unrecycled wastes, the carbon structures can be tailored for processing and reuse in manufacturing of structural composites, building materials such as insulation, carbon dense reactant materials such as activated carbon, and so on. According to the EPA’s estimation, MSW in the United States is approximately 23% paper and paperboard, 12% plastics, 6% wood and 6% is textiles. Thus, this research focused on the feasibility of using the MSW as insulation material for the construction sector. The goal of this work was to determine the range of particle sizes, consolidation ratios, and component blends that can achieve insulation R-values within at least 70% that of traditional blown cellulose fiber. To achieve this goal, we designed the testing matrix based on five different component blends, three different particle sizes, and three different compaction level. An American Society for Testing and Materials (ASTM) method (C-739) was used to measure the R-value of the insulation material. Results showed that, adding more paper component in addition to smaller particle size and loose compaction made the insulation similar to the traditional blown cellulose fiber insulation as the R-value was within a range of 2.5-3.0 per inch.