Passivated Interfaces and Surface Recombination Velocities in Halide Perovskites

Abstract

Surfaces and charge-extracting contacts remain major sources of non-radiative recombination loss; limiting the performance of perovskite PV compared to theoretical limits. We investigate mixed-cation mixed-halide perovskites and demonstrate that, with chemical surface passivation, they can achieve >4 μs minority carrier lifetimes, and >20% external PL quantum yields (PLQY), and nearly single-exponential decay kinetics. This high PLQY observed corresponds to ~97% of the Shockley-Queisser theoretical quasi-fermi level splitting, a first for MA-free mixed-cation mixed-halide compositions. The high PLQY and long PL lifetimes allow us to measure average surface recombination velocities (SRV) <10cm/s, with a champion low of ~1cm/s (a conservative estimate). We show how such improvements in SRV should lead to an absolute improvement in PCE of >4% even with the best of contact alignments. We investigate different MA-free high bandgap compositions, including bandgaps relevant for tandem applications (1.7-1.8eV), and demonstrate performance improvements across all these compositions with our surface passivation strategy. Lastly, using a combination of surface characterization techniques, we show Lewis base interactions of the passivating agent with the perovskite surfaces.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Ginger, David. 2020-11-27. Passivated Interfaces and Surface Recombination Velocities in Halide Perovskites. https://doi.org/10.2172/1910164

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Self Assembled Monolayers for Passivated Contacts

Passivated contacts mitigate defects typically encountered due metallization of solar cells. We deposit amorphous silicon (a-Si:H) on an oxidized silicon wafer via PECVD and anneal at high temperature to crystallize into polysilicon passivated contact. One drawback is the absorption of the polysilicon between grid fingers, so removal of this material is desirable to maximize Jsc. Alternatively, interdigitated back contact cells rely on a gap between n- and p- fingers, which is commonly etched to ensure electronic isolation. We utilize a self assembled monolayer (SAM) using hexamethyldisilazane (HMDS) as a precursor to pattern and etch amorphous silicon (a-Si:H) and polysilicon without the need for photoresist. Ultraviolet light exposure oxidizes the HMDS by photocleaving the organic groups [1] of the SAM leaving a patterned SiO2. Directly soaking this in TMAH will eventually etch the SAM and the silicon, where the SiO2 serves as an etch mask. Inversely, a dilute HF dip selectively etches this SiO2 and the SAM remains. A subsequent soak in TMAH selectively etches the underlying silicon, where the SAM serves as an etch mask. Importantly, we find that the SAM can remain intact for metallization, where we measure 10 mO-cm2 specific contact resistivity on n-type polysilicon.

passivation↗