Ytterbium Ion Collection on Graphite Plates

Abstract

Surface characterization and analysis of the graphite collection and strike plates was conducted in this report. These plates were from an electromagnetic isotope separation collector that had been irradiated with an ytterbium ion beam. The results of this study are reported along with analysis and discussion of the potential growth mechanism of the ytterbium layer on graphite. It is proposed that directional deposition of ytterbium ions occurs first in the defect regions of the graphite plate. As deposition continues, it leads to the eventual formation of directional globs that elongate and grow into plates, then stacks, and finally into sheets of ytterbium. The ytterbium layer appears to have a definite phase boundary with the graphite layer. It was also determined that during irradiation with the ytterbium ion beam, the sputtered carbon becomes interpolated in the ytterbium surface layer on the graphite plate and has an amorphous microstructure.