High Performance PEFC Electrode Structures

Abstract

Raytheon Technologies Research Center (RTRC) in collaboration with Ion Power Inc. and the University of Arkansas at Little Rock and the FC-PAD consortium executed a project that: (1) developed comprehensive models of oxygen and proton transport in cathode catalyst layers that provided new insights about losses associated with reducing platinum loading to 0.1 mg/cm 2 , (2) designed, fabricated, characterized, and tested cells featuring carbon-supported catalyst layers with low platinum loadings that met efficiency and power density targets set forth by the Hydrogen and Fuel Cells Technology Office, and (3) designed, fabricated, characterized, and tested novel catalyst structures. The modeling efforts produced eight scientific publications that shared new descriptions of oxygen and proton transport in catalyst layers with the broader technical community. The key physical insights from the models are expressed in straightforward algebraic expressions, facilitating easy adoption by other researchers. The models developed during the project explain why resistance to oxygen transport is inversely proportional to interfacial area of platinum – an observation that eluded quantitative explanation for a decade. The models quantitatively predict polarization when measured morphological parameters and transport properties are input. Membrane-electrode assemblies made during the project met stated goals for current at high voltage and power density at rated voltage for transportation fuel cells at the end of budget period 2. High performance was achieved by developing a diffusion layer with low resistance to oxygen transport and a PtCo/C cathode catalyst layer capable of supporting rapid proton and oxygen transport. The project was subsequently directed to curtail experimental work and focus on modeling during budget period 3. Ion Power Inc. developed new expertise in fabricating catalyst layers containing platinum-cobalt catalysts, and processing very thin membranes. The University of Arkansas at Little Rock developed novel nanocolumnar self-supported thin film electrocatalysts that can be grown on carbon supports using a simple high pressure sputter deposition method. The nanocolumnar microstructure provides adequate surface-to-volume ratio for efficient platinum utilization, and the conformal platinum shell with larger crystal grain sizes covering the carbon support surface may eliminate durability issues associated with catalyst dissolution, agglomeration, and carbon corrosion.