Pseudocapacitive Charge Storage in Electrochromic Transition-Metal Oxide Thin Films

Abstract

Electrochromic pseudocapacitive transition-metal oxide materials, such as tungsten oxide, which combine fast response, high energy density, and optical effects, can play a significant role as energy storage materials. Here we investigate the electrochemical kinetics of thin films of tungsten oxide, which turn transparent to sky-blue color in the lithiated state due to the reduction of W 6+ to W 5+ . In this study, we investigated the charge density, charge transfer, ion diffusion, and interfacial behavior upon Li + insertion/de-insertion in WO 3 . The electrochromic thin film's pseudocapacitive and electrical double layer mechanism was differentiated based on the power-law. Faradaic diffusion-controlled process dominates over the surface capacitive behavior at scan rates below 40 mV s –1 . These films exhibit an areal charge density of around 100 mC cm –2 and a capacitance of 80 mF cm –2 , superior to most comparable electrochromic materials and supercapacitors. This work combines electrochromics and energy storage properties and provides a fundamental understanding of pseudocapacitive and electrochromic mechanisms in WO 3 .