Tritium Diffusion in Fe-Al Aluminide Coating Bulk Phases

Abstract

The theoretical investigations of interstitial tritium diffusion pathways in various Al-rich (>60% at. Al) iron aluminide coating phases found that in FeNiAl 5 tritium prefers to diffuse in between layers, while in Fe 4 Al 13 , tritium prefers to diffuse across layers. In the case of Fe 2 Al x phases, the simulations show that the variable Al content in the channels affects the diffusion behavior of tritium in the channels. For 100% of vacancy, tritium prefers to diffuse at the center of the channel, while for 0% Al vacancy, tritium prefers to diffuse along the channel’s wall. In the case where 50% Al vacancy are present in the channels, tritium can diffuse in a mixed way, with positions oscillating between the channel’s center and wall. However, the large energy barrier involved in this case suggests that tritium diffusion could be correlated with Al diffusion in the channels. While we found that at 600 K interstitial tritium diffuses faster in Fe 2 Al x phases (D Τ ≤10 -11 m 2 .s -1 ), then in Fe 4 Al 13 (D Τ ≈10 -12 m 2 .s -1 ), and finally in FeNiAl 5 (D Τ ≈10 -13 m 2 .s -1 ), we also find that interstitial tritium generally diffuses faster in Fe-Al coating phases than in γ-LiAlO 2 pellets (D Τ ≈10 -14 m 2 .s -1 ).