Magnetostrictive materials for enhanced sensors and electronic components

Abstract

Magnetostriction is a property of magnetic materials that causes them to change their shape or dimensions proportional to their magnetization. Low-cost, mechanically robust magnetostrictive sensors would be valuable for a wide range of applications across the DOE and national security mission space, such as monitoring the internal conditions of pipelines, rapidly detecting high-impedance faults in power lines (e.g. trees touching power lines), or enhancing implantable systems for the human body. Dilute doping (<1 at.%) of rare earth elements (REE) has been shown to amplify the magnetostriction. Furthermore, alloy processing by rapid cooling from high temperature tends to result in texturing and therefore greater magnetostriction values, which bodes well for developing advanced manufacturing approaches significantly less expensive than single crystal growth. The goal of this effort was to develop robust, low-cost magnetostrictive materials compatible with advanced manufacturing techniques to exploit the rapid cooling of these approaches while retaining the ability to produce fully dense structures. To be useful as a sensor or actuator the coercivity of the material needs to be minimized so that there is minimal magnetic hysteresis. Employing a small scale laser powder bed fusion (L-PBF) system, specimens of Fe-Ga-Ce were built from alloy powder which had a magnetostriction of 289 ppm along the build direction and 197 ppm perpendicular to the build direction. These values are not far from the 310-350 ppm observed in single crystals of Fe-Ga. The results of the series of samples run suggest this is a very promising route for REE doping to higher levels, especially if the powders can be produced using far from equilibrium approaches such as ultrasonic atomization. The promising results from applying additive manufacturing techniques to these materials, particularly the inexpensive Fe-Al system, has potential for inexpensive high-performing magnetostrictive parts producible at large scales for low-cost sensors.