Characterizing CA{sub 2} and CA{sub 6} using ELNES

Abstract

Calcium aluminates, compounds in the CaO-Al{sub 2}O{sub 3} phase system, are used in high-temperature cements and refractory oxides and have wide range of potential technological applications due to their interesting optical, electrical, thermal, and mechanical properties. They are used in both crystalline and glassy form; the glass is an isotropic material while the crystalline materials may be highly anisotropic. This paper will consider two particular crystalline materials, CA{sub 2} and CA{sub 6}, but the results should be applicable to all calcium aluminates. Although CA{sub 2} and CA{sub 6} crystals contain the same chemical species, Ca, Al, and O, the coordination and local environments of these species are different in the two structures and hence they show very different energy-loss near-edge structures (ELNES) when examined by electron energy-loss spectroscopy (EELS) in the TEM. The data obtained using ELNES can effectively provide a fingerprint for each compound and a map for their electronic structure. Once such fingerprints are obtained, they can be used to identify nano-sized particles/grains or material at interfaces and grain boundaries. In the present study, the local symmetry fingerprints for CA{sub 2} and CA{sub 6} structures are reported combining experimental spectra with electronic-structure calculations that allow the different features in the spectra to be interpreted. Al-L{sub 2,3} and O-K edge core-loss spectra from CA{sub 2} and CA{sub 6} were measured experimentally using electron energy-loss spectroscopy in a monochromated scanning transmission electron microscope. The near-edge structures were calculated for the different phases using the orthogonalized linear combination of atomic-orbitals method, and took account of core-hole interactions. It is shown that CA{sub 2} and CA{sub 6} structures exhibit distinctive experimental ELNES fingerprints so that these two phases can be separately identified even when present in small volumes. - Graphical abstract: Projection of the CA{sub 2} structure viewed in the [010] direction. Green atoms represent the Ca{sup 2+} ions and blue atoms represent the Al{sup 3+} ions. Two unit cells are outlined..

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Altay, A, Rulis, P, Ching, W -Y, Arslan, I, Guelguen, M A. 2010-08-15. Characterizing CA{sub 2} and CA{sub 6} using ELNES. https://doi.org/10.1016/j.jssc.2010.05.028

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗