Epitaxial Multifunctional Oxide Heterostructures (DOE Final Technical Report)

Abstract

The conducting interface that forms between the two band insulators LaAlO 3 (LAO) and SrTiO 3 (STO) continues to attract tremendous attention nearly 15 years after its discovery. Until recently, most of the work on this system has been done in samples grown in the (001) crystal orientation. More recently, interest has focused on samples grown in the (110) and (111) crystal orientations. While the underlying cubic crystal structure is the same, the lattice symmetry at the interface in each case is different, raising the possibility of different properties. In particular, the symmetry of the Ti atoms at the (111) interface is hexagonal, similar to graphene, leading to predictions of topological properties of the band structure. The major part of this proposal is devoted to exploring the properties of (111) LAO/STO interfaces and (111) (La 0.3 Sr 0.7 )(Al 0.65 Ta 0.35 )/STO (LSAT/STO) interfaces, where we have recently discovered interesting new effects.