SiC cladding corrosion and mitigation

Abstract

Silicon carbide (SiC) is a leading candidate for accident tolerant fuel. Testing of SiC in autoclaves at 360 C. degrees in simulated coolant resulted in little corrosion. However, testing of SiC tubes in the Massachusetts Institute of Technology (MIT) reactor manufactured in the same way had unacceptable corrosion levels. This in-reactor SiC corrosion issue is now being addressed by Westinghouse in tests being carried out at our Churchill, PA facility and in tests in the MIT reactor. The suspected driver for the excessive corrosion is the generation of oxidative water radiolysis products in the core. The MIT reactor was identified as running at H{sub 2} levels of ∼20 to 22 cc/kg coolant (cubic centimeters standard temperature and pressure per kilogram coolant) which were below those normally specified in operating pressurized water reactors (PWRs) of 25 to 50 cc/kg. Hydrogen is used to react with the radiolysis products to reduce them to water. The current MIT reactor tests will be run at H{sub 2} concentration levels of ∼50 cc/kg. The applicability of this approach has been supported by recent papers in the literature. Parallel testing at Churchill is being carried out to verify the efficacy of this approach using autoclaves operating at 345 C.degrees with H{sub 2}O{sub 2} injection to simulate the water radiolysis products. Various concentrations of H{sub 2} are being tested to determine the effect on SiC corrosion rate. Further studies are underway to investigate the effects of different SiC fabrication and structural parameters and to optimize for improved corrosion performance. This paper compares the results of the corrosion tests in the MIT reactor and the autoclave tests with H{sub 2}O{sub 2} injection and the effect of H{sub 2} injection on the SiC corrosion rate. The results of the autoclave tests with H{sub 2}O{sub 2} addition indicate that corrosion rates for SiC can be achieved that are much higher than those achieved in a reactor. It appears that the use of H{sub 2}O{sub 2} addition in flow through loops to simulate the corrosion rate of SiC samples in reactor is feasible. The use of H{sub 2} addition to reduce the corrosion rate in-reactor of SiC appears to be feasible.