Microstructural Modeling of the α + β Phase in Ti-6Al-4V: A Diffusion-Based Approach

Abstract

Complex heat treatment operations and advanced manufacturing processes such as laser or electron-beam welding will see the metallic workpiece experience a considerable range of temperatures and heating/cooling rates. These intrinsic conditions will have a significant bearing upon the microstructure of the material, and in turn upon the thermo-mechanical properties. In this work, a diffusion-based approach to model the growth and shrinkage of precipitates in the alpha + beta field of the common titanium alloy Ti-6Al-4V is established. Further, the numerical model is extended using a JMA-type approach to explore the dependency of the beta-transus temperature on extremely high heating rates, whereby dissolution alone is too slow to accurately describe the alpha to beta-phase transformation. Experimental heat treatments at rates of 5, 50, and 500 °C/s were performed, and metallographic analysis of the samples was used to validate the numerical modeling framework predictions for lamellar shrinkage, while data from the literature has been used to evaluate the numerical modeling framework for the growth of equiaxed microstructures. The agreement between measurements and numerical predictions was found to be good.