NSUF Report EBSD analyses on metallic fuel samples: Tips and improvements in sample preparation

Abstract

EBSD (Electron Backscatter Diffraction) is an analytic technique used to evaluate the microstructure of a specimen. It can be used to evaluate interesting crystallographic data ranging from grains size to grain orientation, from grain boundaries to stresses. Moreover, in the field of nuclear materials EBSD can aid in estimating properties important for reactor performance, such as dislocation and residual strain [1]. EBSD patterns are generated by focusing a stationary electron gun on the specimen and detecting the backscatter electrons that satisfy Bragg conditions, and thus are diffracted by the crystal planes forming the so called Kikuchi bands. These bands correspond to each of the lattice diffracting crystal planes and are detected on a phosphor screen via a low-light CCD camera [2]. The patterns are generated within a small interaction volume located at a depth of less than 50-100 nm. Because of this, the data quality is extremely sensitive to the integrity of the crystallographic lattice order at the surface of the sample and thus to sample preparation and to oxidation [3]. While conventional sample preparation methods are widely used in materials science, they often do not lead to quality electron backscatter patterns needed for the characterization of nuclear materials [4]. This has been related by many authors to the challenges associated with handling radiological specimens, their rapid oxidation, and artifacts in such samples (e.g. high number of defects, precipitates and/or porosities) [4-8]. EBSD, however, can be an invaluable technique to evaluate microstructural evolution during fabrication and after irradiation at the required mesoscale for model and simulation. It also provides important information on grain structure necessary to understand irradiation effect, such as grain subdivision. Thus, it is of paramount importance to further the application of this technique to nuclear materials and especially irradiated fuels.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Di Lemma, Fidelma Giulia. 2022-05-01. NSUF Report EBSD analyses on metallic fuel samples: Tips and improvements in sample preparation. https://doi.org/10.2172/2314983

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Evaluating transient fission gas release in high burnup light water reactor fuel during loss of coolant accident conditions via new capabilities

In this work, the role of transient fission gas release (tFGR) in the cladding burst behavior of high burnup fuel during a loss-of-coolant accident (LOCA) in commercial light water reactors was further investigated via the use of a new apparatus. During the LOCA-related temperature ramps of high burnup fuel, the release of fission gases exceeds the steady-state release observed under normal operating conditions. An enhancement was made to the Oak Ridge National Laboratory Severe Accident Test Station (SATS) to probe the various factors influencing tFGR. Experiments were performed on commercially irradiated, zirconium-clad uranium dioxide fuel, and this paper details the design of the experimental setup, the initial test results, and the subsequent post-test analyses. Notably, the first test on high burnup fuel demonstrated a LOCA-relevant tFGR of 5.3% from an unpressurized fuel segment. The ultimate tFGR was 10.7% for beyond LOCA conditions. A follow-up test on similar fuel revealed a tFGR of 12.6% under comparable conditions. Microstructural analysis and an analysis of the released gas provide some insight regarding the source of tFGR in the fuel. Finally, a grain boundary bubble model may aid in the interpretation of the results and offer a guide for future work.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Characterization of ceramic fuel powder packing fractions to support INFLUX

Triply periodic minimal surface (TPMS)-based structures show marked potential in novel nuclear reactor fuel designs, as their high surface area-to-volume ratio increases the efficiency of heat transfer out of the fuel, enabling safer, more innovative reactor designs. This milestone report addresses the role of dUO 2 powder processing route on the fill behavior of TPMS-based cladding shells to understand and advance the feasibility of manufacturing TPMS-based nuclear fuel forms. dUO 2 powder was processed through either a dry granulation route, varying consolidation pressure, or through milling, varying milling time, milling method and milled size distribution. The lowest tapped bulk densities (TBD), but best powder flowabilities, were obtained when testing unprocessed dUO 2 powder which was prone to self-agglomeration and formed low-density spheroids. The highest TBD and lowest flowabilities were obtained when using powder produced by hammer-milling dUO 2 powder to pass through a 200-mesh sieve, which led to particles with angular morphologies. Powder produced by dry granulation exhibited TBD that varied according to the consolidation pressure used to form the initial pellets and exhibited improved flowabilities when compared to hammer-milled material. Because of the large span of granule sizes formed as well as the irregular shape associated with the granules, a packing fraction of 0.69 was achieved, exceeding the analytical solution for random close packing of mono-sized spheres. TPMS polymer shells were loaded with unprocessed, granulated, and hammer-milled dUO 2 powders, and their qualitative packing behaviors were analyzed using x-ray computed tomography (xCT). TBDs calculated after loading TPMS polymer shells were 10-20% lower when compared to tapped bulk density measurements taken in a glass graduated cylinder, indicating a non-trivial impact on the tapped bulk density of either the TPMS channel size, TPMS channel surface material, powder cohesiveness, or a combination of the two parameters. A metallic zircaloy-4 TPMS shell will be loaded with hammer-milled dUO 2 powder upon receipt of the shell from Oak Ridge National Laboratory (ORNL) and shipped to Idaho National Labs (INL) for subsequent hot isostatic pressing (HIP) densification experiments.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗