Neutron and photon in-vivo materials characterization at the evolving plasma-material interface in plasma-burning fusion environments

Abstract

This report includes the first set of MOSS data collected in the context of fusion-relevant plasma-material interactions. The data collected show that the surface curvature and stress irreversibly change during low-energy deuterium ion irradiation. This holds for both tungsten thin films, bulk tungsten, and single-crystal silicon. Meanwhile, argon irradiation did not produce this same effect. The surface morphology of the exposed samples was virtually identical regardless of gas species. There were, however, some surface chemistry differences between argon-exposed and deuterium-exposed samples, mainly concerning the oxide states of the W4f XPS signal. The changes in surface chemistry could be due to hydrogen dynamics on the tungsten surfaces, though further investigation will be required with in-situ irradiation and analysis. The changes in surface stress could also not be explained by temperature alone, as the temperature reached during the ion irradiations was too low to induce non-elastic strain. With this in mind, deuterium retention in the materials could change the surface curvature and stress. To confirm this, further work will be needed to quantify the change in curvature and relate it to ion flux, fluence, and deuterium retention. Unfortunately, when this work was conducted, the experimental setup for thermal desorption spectroscopy was not operating correctly, and that work could not be included in this dissertation. Despite experimental difficulties, this work shows the first results of a promising technique to study deuterium dynamics in tungsten-based reconstituted thin films.