Understanding the microstructural evolution of hypersaline cemented paste backfill with low-field NMR relaxation

Abstract

Highlights: • Microstructural evolution of CPB, prepared with tap and hypersaline water, is monitored using low-field NMR relaxometry. • T{sub 1} and T{sub 2} NMR relaxation measurements compared with mechanical strength via UCS tests • Hypersaline mixing water results in slower structural evolution and lower mechanical strength. Cemented paste backfill (CPB) comprising mineral tailings, binders and mixing water is an important potential support material in the mining industry. As the mechanical properties of CPB are significantly influenced by its microstructural characteristics the development of measurement tools to better understand its pore structure evolution is important for its increased utilisation. This study reports the application of low-field nuclear magnetic resonance (NMR) relaxation time measurements to characterise the microstructural evolution of CPB materials over 56 days of hydration, contrasting common tap water and hypersaline water (~22 wt% salt) as mixing water. Distinct NMR relaxation time populations were evidenced within each CPB sample, revealing the presence of both capillary (T{sub 1,2} ≈ 10 ms) and gel pore water (T{sub 1,2} ≈ 300–500 μs), with time-dependent relaxation measurements facilitating characterisation of capillary pore structure evolution over the hydration period assessed. Hypersaline samples demonstrated a time-lag in this measured capillary pore evolution, relative to those hydrated with tap water, while pore structure evolution rates were observed to increase with increased CPB binder content. Further, both T{sub 1} and T{sub 2} NMR relaxation times were found to correlate with the uniaxial compressive strength of the CPB materials investigated, facilitating the formulation of a predictive correlation function between NMR relaxation characteristics and mechanical properties.