Formation, structure, and thermal stability evolution of ternesite based on a single-stage sintering process

Abstract

Highlights: • The synthesis of high-purity ternesite based on a single-stage sintering process was firstly studied. • The formation mechanism and crystallization behaviour of ternesite during sintering were investigated. • The structure perfection and symmetry of ternesite crystals were increased with its growth. • The growth and structural development of ternesite crystals during sintering resulted in a higher thermal stability of itself. Ternesite was prepared via a single-stage solid-state reaction from stoichiometric quantities of the CaCO{sub 3}, SiO{sub 2} and CaSO{sub 4}·2H{sub 2}O precursors. In this paper, the formation, structure, and thermal stability evolution of ternesite during sintering were investigated ex situ after quenching. The optimal sintering temperature for the formation of high-purity ternesite was approximately 1200 °C for 12 h, of which the purity level can reach as high as 96.3%. The results from scanning electron microscopy analysis suggest that the formation of ternesite benefited from the preformation of the intermediate silicate phase. Increasing the sintering temperature from 1100 °C to approximately 1250 °C was favourable for the growth of ternesite crystals, and a prolonged duration can also promote this behaviour. The structural perfection and symmetry of ternesite crystals increased with its growth, which was demonstrated by a multimethod approach. By means of thermal analysis, the growth and structural development of ternesite crystals during sintering eventually resulted in a higher thermal stability.