Quantitative microstructural investigation of 3D-printed and cast cement pastes using micro-computed tomography and image analysis

Abstract

Highlights: • Processing alters the microstructure in 3D-printed lamellar cubic element. • A unique patterned and connected pore microstructure network exists. • Micro-channels are connected through micro-pores present at interfaces regions. • Three distinct pore volume domains exists in hardened microstructure. • Volume and frequency of pore, hydrated, and unhydrated clusters are dissimilar. Microstructural phases and mechanical properties of lamellar 3D-printed and cast hardened cement paste (hcp) elements were investigated using a lab-based X-ray microscope at two levels of magnification (0.4× and 4×). K-means clustering was used for quantitative image analysis. The entire volume of intact 3-days-old 3D-printed and cast hcp elements was characterized at 0.4× magnification. Three microstructural features (macro-pores, micro-channels, and interfacial micro-pores) were found to reside in three distinct pore size domains. The largest pores of the 3D-printed element were larger than the largest pores of the reference cast hcp element. Moreover, the smallest pore sizes of the 3D-printed element were found to be smaller than those present in the cast counterparts. Micro-channels were found to be connected to one another through the micro-pores present at interfacial regions, indicating the presence of a uniquely patterned and interconnected pore network. The role of locally weak and porous interfaces on mechanical response and fracture properties is discussed.