ANS MiNES 2023 Poster

Abstract

The dynamic mechanical properties of four varieties of high purity graphite as well as the depth of penetration (DoP) of a small-scale shaped charge into these grades was experimentally determined. The grades chosen were PCEA, NBG-18, and NBG-25. These grades provide a wide range of physical properties: in density from 1.80 – 1.85 g/cc, in maximum particle size from 10s to 1000s of µm, and in porosity from 18% to 20%. The quasistatic and dynamic compressive strengths of each grade were determined and correlated to their physical properties. The split Hopkinson pressure bar experiments showed both the dynamic strength and dominant shear failure mechanisms. A small scale shaped charge was used to compare the resistance of graphite to hypervelocity jet impacts: the Teledyne RP-4. The RP-4 has a 1.01” outer diameter and 3.44 g of RDX with an RP-80 booster (86 mg PETN + 123 mg RDX). A select number of samples were analyzed using X-Ray Computed Tomography (XCT), allowing for the full characterization of the undisturbed wound channel. A selection of other samples were physically sectioned and wound channels mapped from the sections. In addition to DoP, the wound geometry was characterized in terms of total volume and diameter at different depths. The wound channel characteristics for each grade were correlated to the compressive strengths and physical properties. In several of the test samples, the wound channel diameter was smaller than the diameter of the shaped charge slug just behind where the slug had penetrated the sample. These results indicated that the wound geometry was dependent on the compressive hysteresis behavior of graphite.