Massive all-atom analysis of 2D materials with quantum properties (Final report)

Abstract

Improvements in microscopy have enabled the acquisition of data at a scale that is difficult to process manually, making automated machine learning approaches to analyzing experimental images essential. In this project, we developed and applied machine learning (ML) workflows for atomic resolution scanning transmission electron microscopy (STEM) images. This development included improving both methodology as well as generating user-friendly codes. We developed machine learning architectures which, after training, automatically identify the location and types of defects throughout a material. We used these data to produce class-averaged images of 2D atomic coordinates with up to 0.3 pm precision, uncovering the structure and oscillations of long-range strain fields around point defects in WSe 2-2x Te 2x . We also resolved a long-standing problem in this field in the training of ML models, a lack of labeled experimental data, by developing a cycle-GAN that transformed simulated-generated labeled data into labeled data indistinguishable from experiment and therefore suitable for training. This removed the remaining parts of the ML data processing workflow where human intervention was still critical and therefore a bottleneck to working at scale. Codes have been developed and released for this full machine learning workflow. ML approaches to partially automate STEM acquisition were also developed. Finally we applied ML and other advanced data processing methods to several materials science problems in two-dimensional materials, including studying the evolution of hyperuniformity with defect concentration in WSe2, understanding phase transformations in transition metal dichalcogenides during in-situ heating in the STEM, and exploring how 2D interfaces transform from twisted into aligned structures.