Proton-Conducting Solid Oxide Electrolysis Cells for Large-scale Hydrogen Production at Intermediate Temperatures

Abstract

Proton-conducting electrolyte based SOECs offer potential for operation at low to intermediate temperatures. Although yttrium-doped barium zirconate (BZY) and ceria-doped barium zirconate (BCY) have conductivity of 0.01 and 0.017 S.cm -1 respectively at 650C in comparison to the conductivity of 0.015 S.cm -1 for 8-YSZ at 850°C, there remains technology gaps and research needs related to understanding of chemical and structural stability in oxidizing and/or reducing atmospheres at intermediate temperatures, material processing and densification techniques, high polarization losses, and electrode poisoning due to intrinsic and extrinsic gas phase contaminants. Synthesis methods have produced proton-conducting materials and cells that met degradation rate targets, showcasing stable hydrogen production. Improved performance was evident in the HSOEC cell, achieving higher hydrogen production at a lower operating temperature compared to standard cells. Collaborations with multiple research facilities ensured scaling up of synthesis processes and milestone achievements for large-scale manufacturing. Assessment of contaminants revealed their adverse effects on electrode performance and structural stability. Contaminants like Cr and Si compounds, in high humidity, degraded electrodes by forming stable silicate and chromates, inhibiting active surface reactions. Getter materials showed promise in capturing contaminants, suggesting potential for mitigation.