High Performance Flow Battery with Inexpensive Inorganic Reactants: DAYS Program (Final Technical Report)

Abstract

RTRC’s DAYS projects focused on new flow battery (FB) chemistries for long duration energy storage: one that pairs aqueous polysulfide and manganese active materials in strongly alkaline electrolytes (S/Mn); another explores ligand-modified metal (LMM) chemistries in moderate pH electrolyte conditions. The S/Mn chemistry met durability targets by running for over 500 cycles and 1000 hours. Combined with this durability, power densities of up to 60 mW/cm2 at 80% round-trip efficiency, and exceptionally low-cost S and Mn active materials, the S/Mn FB offers a pathway to meeting the <5¢/kW-hr levelized cost of storage (LCOS) target first proposed by the DAYS Program and accepted by the DOE Energy Storage Grand Challenge. The LMM chemistry made impressive progress as well, including durability tests that retained performance over 600 hours of cycling. Cell optimization allowed this chemistry to operate as high as 500 mW/cm2 at 80% round-trip efficiency, nearly 10x the power density of S/Mn and comparable to the power density achieved in RTRC’s flow battery stacks using acidic vanadium battery solutions. This enabled the LMM chemistry to also offer a pathway to the <5¢/kW-hr LCOS DAYS and DOE targets. The promising results from the LMM chemistry have led to a recent DOE AMO award to advance the technology to a 5 kW, 20 kW-hr prototype.