Solvent-Mediated, Reversible Ternary Graphite Intercalation Compounds for Extreme-Condition Li-Ion Batteries

Abstract

Traditional Li-ion intercalation chemistry into graphite anode exclusively utilizes the co-intercalation-free or co-intercalation mechanism. The latter mechanism is based on ternary graphite intercalation compounds (t-GICs), where glyme solvents were explored and proved to deliver unsatisfied cyclability in LIBs. Herein, we report a novel intercalation mechanism, that is, in-situ synthesis of t-THF-GICs in the tetrahydrofuran (THF) electrolyte via a spontaneous, controllable reaction between binary-GICs and free THF molecules during initial graphite lithiation. The spontaneous transformation from b-GIC to t-GIC, which is different from conventional co-intercalation chemistry, is characterized and quantified via operando synchrotron X-ray and electrochemical analyses. The resulting t-GIC chemistry obviates the necessity for complete Li-ion desolvation, facilitating rapid kinetics and synchronous charge/discharge of graphite particles even under high current densities. Consequently, the graphite anode demonstrates unprecedented fast charging (1 min), dendrite-free low-temperature performance, and ultralong lifetimes exceeding 10,000 cycles. Full cells coupled with layered cathode, display remarkable cycling stability upon a 15-min charging and excellent rate capability even at -40 °C. Furthermore, our chemical strategies are shown to extend beyond Li-ion batteries to encompass Na-ion and K-ion batteries, underscoring their broad applicability. Our work contributes to the advancement of graphite intercalation chemistry and presents a low-cost, adaptable approach to achieving fast-charging and low-temperature batteries.