Nuclear fuels for transient test reactors

Abstract

Transient test reactors with the ability to test fissile specimens under extreme conditions have been crucial tools in the development of nuclear technologies. Less than 10 unique facility designs have ever been constructed, most of which remain operational today and still use the original nuclear fuel constructed for them more than 40 years ago. Historic fuel systems for transient test reactors vary in significant ways which have marked influences on reactor capabilities. Eventually, new fuel will be needed to support the longevity of transient test reactor missions. This paper reviews precedent transient reactor fuel systems in the context of their unique requirements. A few key conclusions are illustrated by comparing and contrasting these transient test reactors. Fuel composites which are mostly graphite can enable transient reactors with very high neutron fluence capability (>2E16 n/cm 2 ) and are amenable to longer “shaped” transients but cannot achieve pulses <10 ms in duration. Reducing the graphite-to-uranium ratio can yield a very narrow pulse capability but delivers less fluence and requires cores with considerably more fissile material. Designs based on uranium dioxide (UO 2 ) make use of readily available materials to create compact cores with narrow pulse width capabilities but with moderate neutron fluence capabilities (~2E15 n/cm 2 ). Uranium zirconium hydride (U-ZrHx) is a well-established fuel system for pulsing reactors which has been intermittently manufactured throughout the decades. U-ZrHx offers similar capabilities to UO 2 designs in terms of nuclear kinetics, but with about half the fluence capability (~1E15 n/cm 2 ). An evolution of the UO 2 system, termed “ternary ceramic” fuel, shows that dispersing UO 2 in zirconium oxide and calcium oxide can increase fluence capability greatly (~7E15 n/cm 2 ), but is not presently a commonly available fuel form. A unique composite of UO 2 and beryllium oxide (UO 2 -BeO) can be used to create a core with similar kinetics and compact core geometry as U-ZrHx designs, but with significantly higher fluence capability (~6E15 n/cm 2 ). Like ternary ceramic fuel, newly fabricated UO 2 -BeO would require reestablishing its historic manufacturing process which would be further complicated by the health hazards associated with beryllium. In conclusion, like most engineering problems, there is no perfect solution, but this paper outlines the advantages and disadvantages of candidate fuel options to help guide detailed evaluations.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Woolstenhulme, Nicolas, Evans, Jordan, Chipman, Andrew, Armstrong, Robert. 2024-04-19. Nuclear fuels for transient test reactors. https://doi.org/10.1016/j.anucene.2024.110519

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Evaluating transient fission gas release in high burnup light water reactor fuel during loss of coolant accident conditions via new capabilities

In this work, the role of transient fission gas release (tFGR) in the cladding burst behavior of high burnup fuel during a loss-of-coolant accident (LOCA) in commercial light water reactors was further investigated via the use of a new apparatus. During the LOCA-related temperature ramps of high burnup fuel, the release of fission gases exceeds the steady-state release observed under normal operating conditions. An enhancement was made to the Oak Ridge National Laboratory Severe Accident Test Station (SATS) to probe the various factors influencing tFGR. Experiments were performed on commercially irradiated, zirconium-clad uranium dioxide fuel, and this paper details the design of the experimental setup, the initial test results, and the subsequent post-test analyses. Notably, the first test on high burnup fuel demonstrated a LOCA-relevant tFGR of 5.3% from an unpressurized fuel segment. The ultimate tFGR was 10.7% for beyond LOCA conditions. A follow-up test on similar fuel revealed a tFGR of 12.6% under comparable conditions. Microstructural analysis and an analysis of the released gas provide some insight regarding the source of tFGR in the fuel. Finally, a grain boundary bubble model may aid in the interpretation of the results and offer a guide for future work.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Characterization of ceramic fuel powder packing fractions to support INFLUX

Triply periodic minimal surface (TPMS)-based structures show marked potential in novel nuclear reactor fuel designs, as their high surface area-to-volume ratio increases the efficiency of heat transfer out of the fuel, enabling safer, more innovative reactor designs. This milestone report addresses the role of dUO 2 powder processing route on the fill behavior of TPMS-based cladding shells to understand and advance the feasibility of manufacturing TPMS-based nuclear fuel forms. dUO 2 powder was processed through either a dry granulation route, varying consolidation pressure, or through milling, varying milling time, milling method and milled size distribution. The lowest tapped bulk densities (TBD), but best powder flowabilities, were obtained when testing unprocessed dUO 2 powder which was prone to self-agglomeration and formed low-density spheroids. The highest TBD and lowest flowabilities were obtained when using powder produced by hammer-milling dUO 2 powder to pass through a 200-mesh sieve, which led to particles with angular morphologies. Powder produced by dry granulation exhibited TBD that varied according to the consolidation pressure used to form the initial pellets and exhibited improved flowabilities when compared to hammer-milled material. Because of the large span of granule sizes formed as well as the irregular shape associated with the granules, a packing fraction of 0.69 was achieved, exceeding the analytical solution for random close packing of mono-sized spheres. TPMS polymer shells were loaded with unprocessed, granulated, and hammer-milled dUO 2 powders, and their qualitative packing behaviors were analyzed using x-ray computed tomography (xCT). TBDs calculated after loading TPMS polymer shells were 10-20% lower when compared to tapped bulk density measurements taken in a glass graduated cylinder, indicating a non-trivial impact on the tapped bulk density of either the TPMS channel size, TPMS channel surface material, powder cohesiveness, or a combination of the two parameters. A metallic zircaloy-4 TPMS shell will be loaded with hammer-milled dUO 2 powder upon receipt of the shell from Oak Ridge National Laboratory (ORNL) and shipped to Idaho National Labs (INL) for subsequent hot isostatic pressing (HIP) densification experiments.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗