Accelerated Synthesis of Ordered Mesoporous Carbons Using Plasma

Abstract

Conventional ordered mesoporous carbon (OMC) production usually requires long processing times in the carbonization step to achieve desired temperatures through controlled ramps. To enable expedited materials discovery, developing advanced manufacturing capability with significantly improved throughput is highly desired. Current approaches for accelerating the synthesis of OMCs include using microwave and Joule heating. However, both methods rely on the introduction of additional components, such as microwave absorbers and electrically conductive agents, within the bulk materials to impart the ability to reach high carbonization temperatures. This work demonstrates accelerated synthesis and functionalization of OMCs through the use of a dielectric barrier discharge plasma, where carbonization can be accomplished within 15 min using 30 W plasma sources, representing more than an order of magnitude increase in polymer-to-carbon conversion kinetics compared to that of a traditionally pyrolyzed analogue. Particularly, the ability of performing rapid carbonization without the use of additional substrates within the OMC precursor systems is advantageous. A systematic investigation of how plasma power, time, and gas atmosphere impact the resulting OMC pore textures and properties is performed, demonstrating the broad applicability of plasma-enabled carbonization methods. Furthermore, we demonstrate that the plasma treatment strategy can be extended to incorporate heteroatoms into the carbon framework by introducing ammonia gas, resulting in OMCs with a nitrogen content up to 4.7 at %, as well as non-Pluronic templating systems for synthesizing OMC with pore sizes larger than 10 nm. As employing a plasma source for materials pyrolysis is an industrially relevant approach, our system can be extended toward scaled synthesis of OMCs with much faster production rates.