UN-SiC TRISO Post Irradiation Examination Developmental Work

Abstract

As part of efforts to strengthen INL?s post irradiation analysis capabilities with non-Advanced Gas Reactor (AGR) tristructural isotropic (TRISO) fuels, two developmental activities were conducted. The first activity was to determine how best to analyze uranium nitride TRISO fuel kernels using electron probe microanalysis, while the second activity focused on developing a method to deconsolidate TRISO fuel particles that have been encased in a silicon carbide matrix. Because these two activities were unrelated, they have been presented separately in this report. Initial EPMA analyses showed nitrogen contents that far exceeded the concentration expected for UN--a line compound. Further examination showed that current literature values for the mass absorption coefficient (MAC) for the N ka X-ray absorbed by U ranged from approximately 1600 to 9500, with most values tending toward 9500. Measuring UN with five different progressively increasing accelerating voltages followed by using the modeling program xMAC suggests the actual MAC is approximately 2115. Additional MAC modifications were required to produce reasonable analytical results. Because of the inaccuracies of necessary MAC coefficients, UN analysis via scanning electron microscopy (SEM) is likely to produce inaccurate results. This is because SEM software does not typically allow the user to alter MACs. Tests have been performed to examine the feasibility of an electrochemical technique to liberate irradiated TRISO fuel from a SiC matrix without damaging the outer pyrolytic carbon layer of the fuel particle. The method is performed by electrochemically exposing the SiC to magnesium metal forming Mg2Si and C. Following exposure, the small SiC samples showed slight mass increases with no evidence of conversion to Mg2Si and C nor obvious degradation of the SiC samples.