Cellulose crystallinity index (CrI) of switchgrass measured by solid-state NMR

Abstract

Here we present a curated dataset of switchgrass cellulose crystallinity index (CrI) measured using solid state nuclear magnetic resonance (NMR) spectroscopy. Seventy-two topline switchgrass lines grown in greenhouse were collected and ground to -20/+80 mesh. The switchgrass was then Soxhlet-extracted with toluene/ethanol for 24 h to remove extractives. The extractives-free switchgrass was holopulped by using peracetic acid at 5 g loading per g biomass and the solution consistency was adjusted to 5% with DI water. Holopulping was conducted at room temperature for 24 h with stirring. The obtained holocellulose was washed excessively with DI water and air-dried at room temperature for 24 h. The dried holocellulose was treated with hydrochloric acid (2.5 M) for 2 h to remove hemicellulose. The isolated cellulose was collected by filtration, rinsed with DI water, and used to analyze cellulose crystallinity by solid-state NMR. The NMR samples were prepared by packing the moisturized cellulose into 4-mm cylindrical Zirconia MAS rotors. Cross polarization/magic angle spinning (CP/MAS) NMR analysis of cellulose was carried out on a Bruker Avance III 400-MHz spectrometer operating at 100.59 MHz for 13C in a Bruker double-resonance MAS probe head at spinning speeds of 8 kHz. The CP/MAS experiments utilized a 5 ms (90°) proton pulse, 1.5 ms contact pulse, 4 s recycle delay and 4000 scans. The cellulose crystallinity index was determined from the areas of the cellulose crystalline C4 signal (δ 86-92 ppm) over the entire C4 regions (δ 79-92 ppm) in the NMR spectra.