Durable and High-Performance SOECs Based on Proton Conductors for Hydrogen Production

Abstract

Proton-conducting solid oxide electrolysis cells (P-SOECs) are a promising technology for cost-effective and efficient production of green hydrogen. Breakthroughs in materials development, optimization of cell structure, and achievement of high performance and durability are essential to significantly increase the commercial competitiveness of these technologies. The main objective of this project is to gain scientific knowledge for the rational design, fabrication, and demonstration of a robust, highly efficient, and low-cost SOEC technology based on a proton-conducting electrolyte membrane for hydrogen production. We focused on better understanding the degradation mechanisms of proton-conducting electrolytes, air electrodes, and catalyst materials under electrolysis mode to develop an effective strategy for rationalizing new materials that are vital for enhancing cell performance and durability. The scope includes enhancing the performance and durability of the electrolyte and electrode materials under realistic operating conditions, developing highly active and robust catalysts to minimize electrode losses while improving tolerance to contaminant poisoning, revealing the mechanism of enhanced activity and stability of the catalyst, and understanding the underlying degradation mechanisms. In addition, various characterization techniques were employed to gain a fundamental understanding of the materials’ behavior and their impact on cell performance, providing vital information to guide materials discovery and cell design. After defect chemistry engineering, the optimized donor and acceptor co-doped electrolytes BaMo/W 0.03 Ce 0.71 Yb 0.26 O 3-δ (BM/W03) showed substantially improved chemical stability against high concentrations of CO 2 and H 2 O compared to the state-of-the-art electrolyte (BaZr 0.1 Ce 0.7 Y 0.1 Yb 0.1 O 3-δ , BZCYYb1711) while maintaining comparable ionic conductivity and ionic transference number. To bypass the inherent trade-off between conductivity and chemical stability, we fabricated a bi-layer electrolyte composed of BZCYYb1711 coated with a highly-stable thin layer of BaHf 0.83 Yb 0.17 O 3-δ (BHYb). This bi-layer electrolyte displayed excellent chemical stability against high concentration CO 2 ; there was no detectable formation of BaCO 3 after exposure to 97% CO 2 (with 3% H 2 O) at 500 °C for 1000 hours and the rate of degradation in resistance was about 0.4% per 1,000 hours (kh). In contrast, the same BZCYYb1711 electrolyte without a BHYb coating degraded significantly under the same testing conditions; the degradation rate was increased to 5.1%/kh. In addition, a triple conducting air electrode Ba 0.9 Pr 0.1 Hf 0.1 Y0.1Co 0.8 O 3-δ (BPHYC) was developed by heavily doping transition metal ions into a proton-conducting material. This air electrode material, composed of 3 distinct phases, exhibits superior electrocatalytic activity due to the synergistic effect from the three component phases. Moreover, an active and durable catalyst, La 2 Ni 0.5 Fe 0.5 O 4+δ (LNF), was developed, showing excellent catalytic activity and contaminant tolerance, with a degradation rate of only 0.49%/kh when exposed to high concentrations of steam and Cr. Finally, single cells were constructed from the best electrolytes, electrodes, and catalyst coatings developed in this project. These cells demonstrated superior high current density at a given cell voltage, high roundtrip efficiency, and remarkable durability (up to 1000 hours of operation).