Time-Temperature-Transformation (TTT) Diagram for a Sludge Batch 9 Glass Composition Based on Coupled-Operation with the Salt Waste Processing Facility

Abstract

The amorphous structure of a glass waste form has the potential to rearrange into crystalline phases at temperatures between the liquidus temperature and the glass transition temperature (Tg). Certain phases that can form will be detrimental to the durability of the glass and it is important to know the conditions that promote devitrification. The canister-centerline-cooling (CCC) profile is used to replicate the area within the center of the Defense Waste Processing Facility (DWPF) canister with the slowest cooling during the initial cool down after pouring, which has the greatest potential for crystallization. Other time-temperature conditions that cause significant changes in either phase structure or phase composition are identified by a time-temperature-transformation (TTT) study. The phase stability of a waste form must be determined as a part of the Waste Acceptance Product Specifications (WAPS) if it is to eventually be stored in a geologic repository. This requires the creation of a TTT diagram and analysis of the Tg, as defined by the Department of Energy (DOE). The previous TTT study for a DWPF glass waste form was completed in 2010 prior to coupled operation with the Salt Waste Processing Facility (SWPF). SWPF transfers two high activity waste streams to DWPF for vitrification: a cesium-containing strip effluent and a stream containing monosodium titanate/sludge solids. These SWPF streams were first transferred to DWPF for vitrification during Sludge Batch 9 (SB9) in 2021. The impact of these SWPF streams on crystallization behavior was not determined in previous studies and the need for data to satisfy WAPS Specification 1.4 for SB9 was identified.