Polymorphism and phase transitions in layered uranium(VI) hydroxides: Ab initio lattice dynamics simulations of UO 2 (OH) 2

Abstract

The phase transitions and thermodynamics of stoichiometric α-, β-, and γ-UO 2 (OH) 2 polymorphs are investigated using density functional perturbation theory. The pressure-induced β(Pbca) → α(Cmca) phase transition is reproduced by calculations, with a volume reduction of ΔV/V = -14.7% similar to experiment. Consistent with observation, a temperature-driven γ(P2 1 /c) → β(Pbca) phase transition is predicted near 533 K. At 298.15K, the computed standard molar heat capacity of α-UO 2 (OH) 2 is C p 0 = 112.1 J mol -1 K -1 , only 1.6% smaller than the value of C p 0 = 113.96 ± 0.12 J mol -1 K -1 measured by calorimetry. C p 0 = 112.4 and 104.8 J mol -1 K -1 are predicted for the β- and γ-UO 2 (OH) 2 polymorphs, respectively. The calculated molar enthalpy and Gibbs energy functions of the α-, β-, and γ-UO 2 (OH) 2 polymorphs are also reported.