Microstructure and diffusion behavior of uranium fuel with minor additives

Abstract

Fission product lanthanides in metallic fuels are known to cause adverse fuel-cladding chemical interaction (FCCI). Tin (Sn) and palladium (Pd) are being explored as the potential additives to reduce or mitigate lanthanide-induced FCCI by forming stable Sn-Ln and Pd-Ln compounds. The current study is an investigation of the fuel alloys, U–4Sn, U–4Sn-4Ln, U–4Pd, and U–4Pd-4Ln (wt. %), and their diffusion behaviors with Fe. Microstructural analysis was performed using scanning electron microscopy (SEM). Further, the binary phases in the UPd and USn alloys are identified as UPd 3 and suspected U 2 Sn, where U 2 Sn is unknown in the literature. The binary phases in the UPdLn alloy are identified as PdLn and Pd-rich Pd-Ln (Pd 4 Ln 3 and Pd 3 Ln 2 ), and in the USnLn alloy is SnLn. Diffusion of Fe with these binary phases is insignificant compared to the diffusion with U. The Ln-induced FCCI can be mitigated by the additives.