High Capacity Step-Shaped Hydrogen Adsorption in Robust, Pore-Gating Zeolitic Imidazolate Frameworks (Final Technical Report)

Abstract

The use of porous adsorbents for the densification of H 2 under relatively mild pressures and temperatures has been long pursued through various avenues of synthetic organic frameworks, namely metal–organic frameworks. However, the overwhelming majority of these materials are macroscopically rigid, exhibiting adsorption–desorption profiles that require appreciable energetic input for their full payload capacity to be stored and subsequently delivered. This reduced “deliverable” capacity is a core inefficiency in the use of porous adsorbents for H 2 densification. Our core mission is to determine a material-based strategy that fundamentally alters the adsorption¬–desorption profile in a manner that obviates these deleterious energetic requirements. Towards this, we have focused on metal–organic frameworks that exhibit “cooperative flexibility”, wherein the material undergoes reversible macroscopic phase changes in response to changes to external temperature and/or adsorbate pressure (i.e., concentration). Where these reversible switches occur between states of disparate enough accessible porosity, cooperatively flexible frameworks can exhibit “step-shaped” adsorption–desorption profiles that enable use of the delivery gaseous payload without the aforementioned additional energy requirements. However, before our work, such the observation of this phenomenon with very weakly adsorbing H 2 had not been observed with the necessary profile and P/T conditions desired for H 2 storage and delivery. During this project we have leveraged a deep understanding of the phase change in family of cooperatively flexible metal–organic frameworks to systematically alter their adsorption–desorption profiles to achieve step-shaped adsorption and desorption of H 2 in a precise P/T regime that enables a high deliverable capacity. Specifically, the thermodynamics of the adsorption/desorption induced phase changes in the baseline framework CdIF-13 (sod–Cd(benzimidazolate) 2 ) were tuned using the mixed-linker, or multivariate, approach to framework derivatization. Follow this, we have pursued a similar approach to tuning the adsorption–desorption profile of a second framework family, MIL-53(Al), which contains only Al(III) and theoretically exhibits a much higher deliverable capacity. In total, our work demonstrates that by first understanding the structural consequences of phase changes in these materials, their behavior can be systematically altered through ligand substitutions, tuning the pressure and temperature conditions at which H 2 is adsorbed and desorbed. Thus, enabling high deliverable capacities of H 2 with minimized energetic requirements.