Statistical fracture behavior of doped UO 2 using a ball-on-ring equibiaxial flexure test method

Abstract

Metal oxide dopants, such as titanium and chromium oxides, have garnered considerable attention for their potential to increase grain size (≥ 30 µm) in UO 2 fuel, purportedly enhancing fission gas retention during reactor operation. Fuel performance is significantly impacted by fuel fracture behavior, so it is important to understand the effects of enhanced grain size and dopant content on UO 2 fuel fracture. UO 2 pellets were doped with 0.1 wt% TiO 2 and 0.3 wt% Cr 2 O 3 to alter density and grain size. Inductively coupled plasma mass spectroscopy measured dopant levels pre- and post-sintering. X-ray diffraction revealed lattice changes and microstrain via Rietveld refinement. Field emission scanning electron microscopy determined grain sizes of approximately 30 µm for TiO 2 doping and 7 µm for Cr 2 O 3 doping. Transverse rupture strength tests were performed on over 30 samples per dataset to obtain characteristic strength and Weibull modulus. Results indicate no statistical difference in fracture strength between 0.1 wt% TiO 2 doped UO 2 and undoped UO 2 , while 0.3 wt% Cr 2 O 3 doped UO 2 exhibited a 20% decrease in fracture strength. Doped UO 2 samples also showed reduced Weibull modulus compared to undoped UO 2 , suggesting increased scatter in fracture strength. This study's findings suggest that titanium and chromium oxide doping in UO 2 , regardless of grain size, induce residual stresses, decreasing fracture strength and increasing variability in fracture behavior.