Adroit Materials Final Scientific/Technical Report kV-class GaN-based Junction Barrier Schottky diodes using ion implantation

Abstract

The primary aim of this research was to develop GaN-based Junction Barrier Schottky (JBS) diodes using an innovative ion implantation process previously established in ARPA-E funded projects. The central focus of our proposed technology revolves around selective area p-type doping, accomplished through the implantation of Mg ions. This approach builds upon our successes in the ARPA-E PNDIODES program, advancing towards commercial device integration. Selective area p-doping plays a pivotal role in realizing the next generation of GaN-based power devices, capable of significantly reducing the carbon footprint in the United States by several million tons. While ion implantation is a well-established technique for achieving selective area doping in SiC and Si materials, its feasibility in GaN had not been demonstrated until now. To fabricate high voltage GaN JBS diodes, we initially created thick n-type drift layers with high carrier concentrations ranging from 5×1015 cm-3 to 2×1016 cm-3 and very high mobilities. Subsequently, Mg ions were selectively implanted to form p-type islands within the n-type drift layer. To reduce electric field crowding at the edge of the diode and to achieve high breakdown voltage, junction edge termination (JTE) and floating field rings (FFRs) were formed using Mg implantation. A high temperature, high-pressure post-implantation annealing process was carried out to activate the implanted Mg ions. As a result, we were able to demonstrate GaN JBS diodes with a breakdown voltage of 915 V and an on-resistance of 0.6 mΩ·cm2. These diodes exhibited a forward bias current density of 1 kA/cm2 at 1.5 V. Subsequently, we achieved GaN JBS diodes with a remarkable breakdown voltage of 1900 V and an on-resistance of 1.9 mΩ·cm2, capable of sustaining a forward bias current density of 0.5 kA/cm2 at 1.5 V. Importantly, the ON and OFF state performance of these GaN JBS diodes surpassed that of Si and SiC-based power diodes reported in existing literature. Lastly, we successfully grew 60 μm thick GaN:Si layers using HVPE with a carrier concentration of approximately 3 to 5×1015 cm-3. Based on simulation and empirical data these devices represent 5 kV GaN JBS power diodes, leveraging the developed processes in this project.