Microstructural features and deuterium diffusion in lithium penta-aluminate pellets under He + and D + ion irradiation

Abstract

Lithium (Li) penta-aluminate (LiAl 5 O 8 ) is investigated as a potential tritium (T) breeding material, with a focus on microstructural response to ion irradiation and deuterium (D) diffusion behavior. Under high-fluence ion irradiation (2 x 10 17 (He + +D + )/cm 2 ) at 773 K, LiAl 5 O 8 exhibits significant disorder on the Li sublattice, as revealed by atomic-resolution scanning transmission electron microscopy, while the Al and O sublattices remain stable, demonstrating strong resistance to structural amorphization. Irradiation induces the formation of platelet-shaped antiphase boundaries (APBs), which may serve as effective D trapping sites. Atom probe tomography suggests the presence of 6 LiD clusters in the mass spectra, though definite conclusions regarding APB composition are hindered by signal overlap and limited data statistics. Time-of-flight secondary ion mass spectrometry reveals that D retention approaches to saturation at 3 x 10 17 (He + +D + )/cm 2 . Isothermal and isochronal annealing studies determine an average diffusivity of 1.6 x 10 -13 at 773 K and an effective activation energy of 0.8 ± 0.1 eV for D migration. Compared to γ-LiAlO 2 , LiAl 5 O 8 demonstrates superior irradiation resistance, minimal Li loss, and enhanced D retention, underscoring its potential as a durable breeder material for T production. In conclusion, these findings provide key insights into the microstructural evolution, defect dynamics, and D retention mechanisms in LiAl 5 O 8 under reactor-relevant conditions.