Discovery, Design, Synthesis and Testing of High Performance Structural Alloys (Final Technical Report)

Abstract

The overarching goal of this project is to understand the phase stability and mechanical behavior of non-stoichiometric multi-principal element alloy (MPEA) materials. In order to identify suitable alloys, we plan to use a combinatorial thin film screening approach, in collaboration with scientists at Lawrence Berkeley National Laboratory who are performing computational work as well as complementary experimental work. Specific tasks within the scope of this project include the fabrication, using thin film deposition from six sputtering targets, of combinatorial samples with multi-dimensional gradients in composition and microstructure. These samples are studied to screen MPEA systems for promising candidate alloys with specific composition(s), based on characterization of composition, structure and mechanical behavior across the thin film. We want to produce single-phase MPEAs with chemical homogeneity in a given thin film region, simple grain structures, and no intermetallic phases present. Gradient films facilitate first-pass screening for desirable characteristics and inform the next stage of work that involves fabrication of bulk MPEA specimens for (tensile) mechanical testing and characterization. To make the bulk alloys, metal (elemental) pieces are melted to form MPEAs, followed by heat treatment to homogenize the composition and microstructure. A subset of alloys is also cast, using vacuum arc melting, to yield larger samples (diameter ~1 cm and length ~5-10 cm) and these allow us to assess viability of scale-up for the alloys in structural applications. Further processing plans include rolling and heat treatment to recrystallize selected bulk MPEAs and grow grains to different extents, in order to investigate size effects in the mechanical behavior of MPEAs. Microspecimen testing will be performed (primarily in tension) to assess the mechanical behavior over a range of temperatures. The deformation microstructure of mechanically tested alloys will be characterized using transmission electron microscopy (TEM) to provide a scientific basis for understanding the structure-property relationships in MPEA mechanical behavior.