This study investigates the photothermal performance of gold nanorods engineered to exhibit longitudinal plasmon resonances at 695 nm, 780 nm, and 970 nm. The work combines synthesis, structural characterization, extinction measurements, numerical modeling, and controlled temperature experiments to quantify how nanorod geometry, resonance tuning, concentration, and chamber shape jointly influence heat generation. Transmission electron microscopy confirms that increasing nanorod aspect ratio systematically shifts the longitudinal plasmon peak toward the near-infrared region. Extinction measurements show strong agreement with theoretical predictions, validating the numerical model across two independent datasets. Three chamber geometries were tested under laser excitation at 640 nm, 808 nm, and 980 nm: an ascending stepped base, a flat base, and a descending stepped base. Without nanorods, the ascending geometry produced the highest efficiency due to enhanced natural convection. After introducing gold nanorods, all geometries exhibited substantial thermal enhancement, with total efficiencies exceeding 20%. The strongest improvement was obtained for nanorods resonant at 780 nm with a mass concentration of 4.6 mg/mL implemented on the descending stepped-base geometry. This performance resulted from the combined effect of spectral overlapping with the 808 nm laser, the highest nanorod concentration, and localized heat accumulation that intensified buoyancy-driven flow. The findings demonstrate that total efficiency is governed by a synergistic interplay between optical resonance, nanoparticle concentration, and macroscopic chamber design, revealing the system-level coupling between nanoscale plasmonic absorption and macroscale heat-transfer phenomena. The results provide a validated framework for tuning nanoscale plasmonic absorbers and optimizing thermal systems for applications requiring efficient light-to-heat conversion.
77 NANOSCIENCE AND NANOTECHNOLOGY↗