Modular Processing of Flare Gas for Carbon Nanoproducts

Abstract

This project demonstrated the technical viability and economic promise of a modular system for converting flared natural gas into valuable carbon nanoproducts (CNPs) through catalytic chemical vapor deposition (CVD). All major project milestones were successfully completed, including reactor design and commissioning, catalyst development, process optimization, technoeconomic analysis, and application testing in concrete systems. The overarching goal was to create a scalable, field-deployable process that valorizes stranded methane by producing high-value carbon materials for use in cementitious composites. At the lab scale, the team designed and built a fluidized bed reactor optimized for use with silica fume-supported nickel catalysts synthesized via atomic layer deposition (ALD). A statistically designed sintering study enabled precise tuning of nickel nanoparticle size, identifying the influence of oxygen partial pressure, time, and temperature on catalyst morphology and performance. These insights allowed the team to target catalyst conditions that maximize carbon nanofilament growth. Subsequent CVD experiments achieved up to 31.8 wt% carbon deposition under optimized conditions, with TEM confirming the presence of nanofilament structures and sustained hydrogen evolution during reaction. Reactor upgrades and empirical fluidization studies supported the development of reliable, repeatable experimental protocols. The modular pilot-scale skid reactor was fully constructed, instrumented, and commissioned. Capable of operating at 675–800°C and pressures up to 290 psig, the system was designed for continuous operation at a carbon production rate of 1 kg/hr. Initial demonstration runs confirmed solids handling, thermal control, and system leak-tightness, although a critical reactor component (the downfeed tube) was inadvertently omitted during final assembly. This omission limited gas–solid contact and prevented meaningful carbon deposition during pilot-scale CVD runs. Nonetheless, the system operated safely under design conditions, and the root cause of performance limitations was clearly identified. Complementary work on UHPC formulations demonstrated that small additions of carbon nanoproducts, including those derived from flare gas, can significantly enhance mechanical performance while preserving workability. A comprehensive study of CNF dispersion techniques and mix design optimization led to a clear protocol for integrating these nanomaterials into concrete. Incorporation of CNPs improved flexural toughness and reduced porosity, supporting their use in high-performance infrastructure applications. A technoeconomic analysis (TEA) confirmed that this process can produce CNP-loaded catalyst material at a levelized cost below $\$$7/kg across a range of catalyst loadings and reaction yields. With estimated market values for the carbon composite product ranging from $\$$14 to over $\$$60/kg, and the ability to blend CNPs into concrete at sub-percent levels with less than 10% added cost, the system presents a compelling economic case. While additional engineering work is needed to optimize fluidization and heat transfer at scale, this project establishes a strong foundation for commercial development. The process is not only technically sound but also economically promising, representing a viable pathway for flare gas mitigation through modular carbon nanomaterial production.