Pushing the Limits: Maximizing Energy Density in Silicon Sulfide Solid‐State Batteries

Abstract

Here, for the first time, we demonstrate a silicon solid-state battery (SSB) architecture that achieves >400 Wh kg −1 , approaching the theoretical limit for silicon-based SSBs. This configuration features a 99.9 wt% micro-Si, a thin sulfide solid electrolyte (SSE), and a high-loading NMC811. Key to these results is strategically selecting and evaluating the processing techniques, whether wet or dry, for the negative electrode, positive electrode and thin sheet-type SSE. Excessive lithium incorporation into the silicon host, beyond the Li 3.75 +Si phase to form a LiSi composite, is essential to match the high capacity of the positive electrode. This SSB achieves over 1000 cycles for a 2 mAh cm −2 with ≈80% capacity retention and 94% capacity retention for 3 mAh cm −2 over 500 cycles at 25 °C. Post analysis identifies the primary capacity decay mechanisms as oxidation at the NMC/SSE interface and structural disruptions within NMC. Meanwhile, the Si electrode maintains a robust solid-electrolyte interphase layer, minimizing capacity decay. This study highlights the necessity for improved NMC coatings, lattice oxygen stabilization, and a durable positive electrode-electrolyte interface to improve the long-term stability of SSBs. Strategies leading to a single-layer pouch cell SSB exceeding 400 Wh kg −1 are developed.