Li Stripping Behavior of Anode‐Free Solid‐State Batteries Under Intermittent‐Current Discharge Conditions

Lee, Kiwoong [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0009000059192586)·Sakamoto, Jeff [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:000000023099462X)
View original source ↗Read source document ↗Export metadata ↓

Abstract

Anode‐free manufacturing holds promise to enable high energy densities and lower Lithium (Li)‐metal solid‐state batteries (LMSSBs). Nevertheless, in contrast to thick Li foil (>50 µm), the stripping capacity of in situ‐formed Li (10–30 µm) is limited due to diminished creep flow, resulting in reduced accessible capacity. This study explores the correlation between stripping capacity and surface roughness of garnet Li 7 La 3 Zr 2 O 12 (LLZO) solid electrolyte. The results reveal that stripping capacity can be enhanced through the surface modification of solid electrolytes. Additionally, this study scrutinizes the stripping behavior of in situ Li under intermittent‐current discharge conditions, which are more relevant to the operational conditions of electric vehicles (EVs). It is demonstrated that, when compared to constant‐current stripping, intermittent‐current stripping effectively suppresses void formation and enhances the stripping capacity of in situ Li by 40%. It is considered that the intermittent current inhibits the accumulation of Li vacancies, thereby delaying the void formation. These findings provide valuable insights into the development of high‐performance anode‐free LMSSBs for EVs.

Explore related subjects

25 ENERGY STORAGEanode-free manufacturingelectrochemistryli-metal anodessolid-state batteriesvoid formation

Keep this discovery

BibTeXRIS

Lee, Kiwoong [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0009000059192586), Sakamoto, Jeff [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:000000023099462X). 2024-04-03. Li Stripping Behavior of Anode‐Free Solid‐State Batteries Under Intermittent‐Current Discharge Conditions. https://doi.org/10.1002/aenm.202303571

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

25 ENERGY STORAGE subjectElectrochemistry subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

NASA NTRSDate not supplied

Lithium Nucleation of Anode-Free Solid-State Batteries with a Dry Compressible Interlayer

Anode-free lithium batteries offer promising advantages, including increased energy density and the ability to address common mechanistic failures within the cell, thus increasing safety. One way that can make this possible is to control lithium nucleation. This could be achieved by reducing the overpotential required and implanting lithophilic nucleation sites in an anodic interlayer to aid in lithium ion transport and plating. The concept has been utilized in solid-state battery systems where electrolytes are solids with further improved safety and structural longevity. In this presentation, we discuss the use of a silver-holey graphene-based anodic interlayer that can be fabricated via direct dry compression without the use of solvent or binder. The addition of silver to the holey graphene matrix creates a route to lithium plating via a lower-energy intermediate. This idea is supported by the presence of a lithium-silver alloy that forms during the activation step. It is understood that the embedded silver acts as a nucleation site for lithium ions, thereby assisting in even plating. This control, combined with the added cushion of the holey graphene itself, can help reduce dendrite formation, ultimately increasing the safety and lifetime of the solid-state batteries.

Solid state batteries↗
DOE OSTI2023

Polycarbonate‐Based Solid‐Polymer Electrolytes for Solid‐State Sodium Batteries

Solid-polymer electrolytes comprised of polypropylene carbonate (PPC) and varied sodium bis(fluorosulfonyl)imide (NaFSI) salt concentrations are investigated for implementation as a conductive solid polymer electrolyte into solid-state cathode composites utilizing a sodium-layered oxide active material. The ionic conductivity generally increases with NaFSI salt content, reaching ≈1 mS cm −1 at 80 °C at the highest salt concentration (PPC:NaFSI = 0.5:1). Through an all-in-one slurry casting method, Na 2/3 Ni 1/3 Mn 2/3 O 2 cathode composites are fabricated in which the dispersed PPC electrolyte acts as the primary binder. Enabled by a bilayer polymer electrolyte system, cycling performance with the PPC cathode electrolyte is optimized with respect to salt concentration and anode material. The best cyclability is achieved with a moderate salt concentration electrolyte (PPC:NaFSI = 5:1), showcasing an initial capacity of 83 mA h g −1 with a remarkable 80% capacity retention after 150 cycles at C/5 rate and 60 °C. The superior performance of the lower salt concentration electrolyte is attributed to better electrochemical stability, as confirmed by linear sweep voltammetry and online electrochemical mass spectrometry measurements. In conclusion, these results underscore the potential of carbonate-based polymer electrolytes and the importance of balancing electrolyte conductivity and stability in cell design.

25 ENERGY STORAGE↗