2,5‐Dimercapto‐1,3,4‐Thiadiazole (DMCT)‐Based Polymers for Rechargeable Metal–Sulfur Batteries

Bhargav, Amruth [Univ. of Texas, Austin, TX (United States)] (ORCID:0000000217938340)·Manthiram, Arumugam [Univ. of Texas, Austin, TX (United States)] (ORCID:0000000302379563)
View original source ↗Read source document ↗Export metadata ↓

Abstract

Organosulfur materials are a sustainable alternative to the present-day layered oxide cathodes in lithium-based batteries. One such organosulfur material that was intensely explored from the 1990s to early 2010s is 2,5-dimercapto-1,3,4-thiadiazole (DMCT). However, research interest declined as the electrode reactions with DMCT were assumed to be too sluggish to be practical. Armed with the advances in metal–sulfur batteries, we revisit DMCT-based materials in the form of poly[tetrathio-2,5-(1,3,4-thiadiazole)], referred to as pDMCT-S. With an appropriate choice of electrode design and electrolyte, pDMCT-S cathode paired with a Li-metal anode shows a capacity of 715 mA h g −1 and a Coulombic efficiency of 97.7% at a C/10 rate, thus quelling the concerns of sluggish reactions. Surprisingly, pDMCT-S shows significantly improved long-term cyclability compared to a sulfur cathode. Investigations into the origin of the stability reveals that the discharge product Li-DMCT in its mesomeric form can strongly bind to polysulfides, preventing their dissolution into the electrolyte and shuttling. This unique mechanism solves a critical problem faced by sulfur cathodes. Encouragingly, this mechanism results in a stable performance of pDMCT-S with Na-metal cells as well. In conclusion, this study opens the potential for exploring other organic materials that have inherent polysulfide sequestering capabilities, enabling long-life metal–sulfur batteries.

Explore related subjects

2,5-dimercapto-1,3,4-thiadiazole25 ENERGY STORAGEMaterials Scienceelectrochemistrymetal-sulfur batteriesorganopolysulfideorganosulfur batteries

Keep this discovery

BibTeXRIS

Bhargav, Amruth [Univ. of Texas, Austin, TX (United States)] (ORCID:0000000217938340), Manthiram, Arumugam [Univ. of Texas, Austin, TX (United States)] (ORCID:0000000302379563). 2023-06-03. 2,5‐Dimercapto‐1,3,4‐Thiadiazole (DMCT)‐Based Polymers for Rechargeable Metal–Sulfur Batteries. https://doi.org/10.1002/eem2.12446

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

25 ENERGY STORAGE subjectElectrochemistry subjectMaterials Science subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related discoveries

DOE OSTI2023

Design and Synthesis of Cubic K 3−2 x Ba x SbSe 4 Solid Electrolytes for K–O 2 Batteries

Developing K-ion conducting solid-state electrolytes (SSEs) plays a critical role in the safe implementation of potassium batteries. In this work, a chalcogenide-based potassium ion SSE is reported, K 3 SbSe 4 , which adopts a trigonal structure at room temperature. Single-crystal structural analysis reveals a trigonal-to-cubic phase transition at the low temperature of 50 °C, which is the lowest among similar compounds and thus provides easy access to the cubic phase. The substitution of barium for potassium in K 3 SbSe 4 leads to the creation of potassium vacancies, expansion of lattice parameters, and a transformation from a trigonal phase to a cubic phase. As a result, the maximum conductivity of K 3−2x Ba x SbSe 4 reaches around 0.1 mS cm −1 at 40 °C for K 2.2 Ba 0.4 SbSe 4 , which is over two orders of magnitude higher than that of undoped K 3 SbSe 4 . This novel SSE is successfully employed in a K–O 2 battery operating at room temperature where a polymer-laminated K 2.2 Ba 0.4 SbSe 4 pellet serves as a separator between the oxygen cathode and the potassium metal anode. Effective protection of the K metal anode against corrosion caused by O 2 is demonstrated.

25 ENERGY STORAGE↗
DOE OSTI2023

Polycarbonate‐Based Solid‐Polymer Electrolytes for Solid‐State Sodium Batteries

Solid-polymer electrolytes comprised of polypropylene carbonate (PPC) and varied sodium bis(fluorosulfonyl)imide (NaFSI) salt concentrations are investigated for implementation as a conductive solid polymer electrolyte into solid-state cathode composites utilizing a sodium-layered oxide active material. The ionic conductivity generally increases with NaFSI salt content, reaching ≈1 mS cm −1 at 80 °C at the highest salt concentration (PPC:NaFSI = 0.5:1). Through an all-in-one slurry casting method, Na 2/3 Ni 1/3 Mn 2/3 O 2 cathode composites are fabricated in which the dispersed PPC electrolyte acts as the primary binder. Enabled by a bilayer polymer electrolyte system, cycling performance with the PPC cathode electrolyte is optimized with respect to salt concentration and anode material. The best cyclability is achieved with a moderate salt concentration electrolyte (PPC:NaFSI = 5:1), showcasing an initial capacity of 83 mA h g −1 with a remarkable 80% capacity retention after 150 cycles at C/5 rate and 60 °C. The superior performance of the lower salt concentration electrolyte is attributed to better electrochemical stability, as confirmed by linear sweep voltammetry and online electrochemical mass spectrometry measurements. In conclusion, these results underscore the potential of carbonate-based polymer electrolytes and the importance of balancing electrolyte conductivity and stability in cell design.

25 ENERGY STORAGE↗
DOE OSTI2023

Interface Design for High‐Performance All‐Solid‐State Lithium Batteries

All‐solid‐state batteries suffer from high interface resistance and lithium dendrite growth leading to low Li plating/stripping Coulombic efficiency (CE) of <90% and low critical current density at high capacity. Here, in this work, both challenges are simultaneously addressed and the Li plating/stripping CE is significantly increased to 99.6% at 0.2 mA cm −2 /0.2 mAh cm −2 , and critical current density (CCD) of > 3.0 mA cm −2 /3.0 mAh cm −2 by inserting a mixed ionic‐electronic conductive (MIEC) and lithiophobic LiF‐C‐Li 3 N‐Bi nanocomposite interlayer between Li 6 PS 5 Cl electrolyte and Li anode. The highly lithiophobic LiF‐C‐Li 3 N‐Bi interlayer with high ionic conductivity (10 −5 S cm −1 ) and low electronic conductivity (3.4×10 −7 S cm −1 ) enables Li to plate on the current collector (CC) surface rather than on Li 6 PS 5 Cl surface avoiding Li 6 PS 5 Cl electrolyte reduction. During initial Li plating on CC, Li penetrates into porous LiF‐C‐Li 3 N‐Bi interlayer and lithiates Bi nanoparticles into Li 3 Bi. The lithiophilic Li 3 Bi and Li 3 N nanoparticles in LiF‐C‐Li 3 N‐Li 3 Bi sub‐interlayer will move to CC along with plated Li, forming LiF‐C/Li 3 N‐Li 3 Bi lithiophobic/lithiophilic sublayer during the following Li stripping. This interlayer enables Co 0.1 Fe 0.9 S 2 /Li 6 PS 5 Cl/Li cell with an areal capacity of 1.4 mAh cm −2 to achieve a cycle life of >850 cycles at 150 mA g −1 . The lithiophobic/lithiophilic interlayer enables solid‐state metal batteries to simultaneously achieve high energy and long cycle life.

25 ENERGY STORAGE↗