Completing the Ba–As Compositional Space: Synthesis and Characterization of Three New Binary Zintl Arsenides, Ba3As4, Ba5As4, and Ba16As11

Abstract

Three novel binary barium arsenides, Ba3As4, Ba5As4, and Ba16As11, were synthesized and their crystal and electronic structures were investigated. Structural data collected via the single-crystal X-ray diffraction method indicate that the anionic substructures of all three novel compounds are composed of structural motifs based on the homoatomic As–As contacts, with [As2]4− dimers found in Ba5As4 and Ba16As11, and an [As4]6− tetramer found in Ba3As4. Ba3As4 and Ba5As4 crystallize in the orthorhombic crystal system—with the non-centrosymmetric space group Fdd2 (a = 15.3680(20) Å, b = 18.7550(30) Å, c = 6.2816(10) Å) for the former, and the centrosymmetric space group Cmce (a = 16.8820(30) Å, b = 8.5391(16) Å, and c = 8.6127(16) Å) for the latter—adopting Eu3As4 and Eu5As4 structure types, respectively. The heavily disordered Ba16As11 structure was solved in the tetragonal crystal system with the space group P4¯21m (a = 12.8944(12) Å and c = 11.8141(17) Å). The Zintl concept can be applied to each of these materials as follows: Ba3As4 = (Ba2+)3[As4]6−, Ba5As4 = (Ba2+)5(As3−)2[As2]4−, and 2 × Ba16As11 = (Ba2+)32(As3−) ≈ 20[As2]4− ≈ 1, pointing to the charge-balanced nature of these compounds. Electronic structure calculations indicate narrow bandgap semiconducting behavior, with calculated bandgaps of 0.47 eV for Ba3As4, 0.34 eV for Ba5As4, and 0.33 eV for Ba16As11.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Watts, Spencer (ORCID:0009000967121935), Wingate, Lindsey, Bobev, Svilen (ORCID:0000000207804787), Baranets, Sviatoslav (ORCID:0000000334493344). 2024-06-01. Completing the Ba–As Compositional Space: Synthesis and Characterization of Three New Binary Zintl Arsenides, Ba3As4, Ba5As4, and Ba16As11. https://doi.org/10.3390/cryst14060570

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Measurements of the inert Hugoniot and observation of mechanical ignition in Ni(V) + Al reactive multilayers via x-ray diffraction

This study investigates the inert Hugoniot response, mechanical ignition, and reaction dynamics of Ni(V)+Al multilayers during longitudinal, laser-driven shock compression experiments. Ni(V)+Al multilayers, known for their self-propagating exothermic reactions, were subjected to longitudinal stresses exceeding 50 GPa using the laser shock facility within the Dynamic Compression Sector (DCS) at the Advanced Photon Source (APS). In situ x-ray diffraction (XRD) revealed that Ni(V) and Al were not in equilibrium during compression, with stress discrepancies attributed to twinning, grain structure effects, and/or dislocation density. However, the measured inert Hugoniot closely matched prior experimental and computational studies, confirming the utility of XRD for measuring the equation of state of thin, complex materials. Additionally, reaction was observed at significantly higher stresses than reported previously using laser-launched flyers. This discrepancy suggests a strong influence of externally imposed shear stress on reaction thresholds, which likely arose from deviations in flyer planarity during past experiments. Full reaction of the multilayer occurred within 40 ns after shock-wave passage, evidenced by complete melting of the constituents. Eulerian hydrocode simulations replicated experimental conditions, providing insights into equilibrium dynamics and experimental artifacts. The results highlight how even small shear forces facilitate ignition in Ni(V)+Al multilayers at lower stresses.

Crystallography↗

The influence of iron incorporation on the microstructure and crystal chemistry of UO 2 fuel

The incorporation of dopants into UO 2 is of interest for both doped advanced fuel and nuclear forensics research. Suitable forensics dopants, or taggants, for nuclear fuels are ones that do not adversely affect the performance of the parent material while still being traceable during key stages of the fuel’s life cycle. In this paper, we present our efforts to understand the effects of doping UO 2 with Fe 2 O 3 under multiple parameters, such as Fe concentration (0–3000 wppm), sintering temperature (1673 K, 1773 K, and 1973 K), sintering time (2–12 h), and atmosphere (reducing and inert). Here, we investigated densification behavior, microstructure evolution, and lattice defects based on the geometric densities, scanning electron microscopy (SEM), X-ray diffractograms, and Raman spectra. The effect of Fe on the microstructure and crystal chemistry of UO 2 is very complex, especially at the intermediate temperature (1773 K), where we found that densification kinetics are enhanced and that lattice contraction occurs for doping concentrations greater than 1000 wppm Fe.

Crystallography↗

Structural, magnetic and electrical transport properties of YMnAl

The intermetallic compound YMnAl, crystallizing in the cubic C-15 (MgCu 2 -type) structure, was prepared using arc-melting and annealing. Rietveld refinement of the XRD pattern yields a lattice parameter of a = 7.816(1) Å⁠. The system exhibits antiferromagnetic order with a transition temperature of approximately 38 K, along with indications of a spin-glass–like phase. The effective magnetic moment, estimated from Curie–Weiss fitting of the susceptibility versus temperature curve, is 6.06 μ B /f.u. and the Curie–Weiss temperature of −79 K confirming the antiferromagnetic nature. Isothermal magnetization measurements below and above the Néel temperature show no saturation, with a maximum magnetization of 0.09 μ B /f.u observed at an applied field of 9 T. The temperature dependence of resistivity exhibits a negative temperature coefficient, characteristic of dirty metals. Hall effect measurements indicate the absence of an anomalous Hall contribution. The Hall coefficient RH, carrier concentration n, and mobility μ estimated from R XY (H) are -1.05×10 -8 m 3 /C, 5.92×10 26 m -3 and 1.05×10 -3 m 2 /V.s, respectively. Our first-principles calculations indicate that YMnAl in the orthorhombic (Imma) structure has the lowest energy; however, the substitutional disorder occurring during experimental synthesis may favor the formation of the cubic Laves phase.

Crystallography↗