Technical Considerations on MURR Control Blade Design Change and Testing using a New Metal Matrix Composite

Abstract

The University of Missouri Research Reactor (MURR) is one of six research reactors, including a critical facility, that are pursuing conversion as part of a collaboration with the U.S. Department of Energy National Nuclear Security Administration Material Management and Minimization Office of Reactor Conversion and Uranium Supply, under the U.S. High Performance Research Reactors (USHPRR) conversion project. Five of the six USHPRR are planned to convert from highly enriched uranium (HEU) fuel using a low-enriched uranium (LEU) high assay monolithic alloy of uranium-10 wt% molybdenum (U-10Mo). As part of the conversion safety analysis, it is necessary to demonstrate the safety performance of the proposed core fueled with LEU as compared to the current HEU cores. The MURR reactor is planning to switch to a new control blade design that uses a metal matrix composite of boron carbide (B 4 C) and aluminum as the absorber in place of Boral®. Since MURR is expected to adopt the new metal matrix composite control blade design prior to conversion, the impact of the new blade design on the neutronics characteristics of the MURR cores for conversion are analyzed in this work through updates to incorporate the changes to the blade design in conversion models as they directly impact the LEU conversion safety analysis. The quantitative comparison shows that the neutronics and thermal hydraulic behavior of one metal matrix composite blade replacing a Boral blade is comparable for the two example MURR LEU and HEU cores states considered. Geometrical changes in the metal matrix composite blade design, combined with a 4% increase in areal boron density, showed local heating effects up to 20% higher than the Boral design. As expected, the metal matrix composite showed slightly lower heat depositions and absorber region temperatures for the LEU cases compared to HEU. Although this analysis was comparative for a single blade, maximum control blade temperatures for both Boral, metal matrix composite, and HEU/LEU remained below 100 °C, though additional analysis at a core level could differ. A qualitative irradiation behavior assessment concludes that the mechanisms that may drive swelling and blistering in the current Boral design are eased by the adoption of the metal matrix composite design. The work concludes that the two blade designs are essentially equivalent with regards to neutronics, thermal hydraulics, and expected material behavior under irradiation. However, due to the geometrical changes to the blades including redesigned and thinner cladding, new testing and increased surveillance for distortion and swelling are recommended to confirm the performance of the metal matrix composite control blade design. Where testing is completed prior to conversion, the only anticipated impacts on conversion to LEU U-10Mo fuel would be the need for models and safety analysis incorporating the metal matrix composite control blades.