Direct observation of strain-enhanced hydrogen segregation and failure at high-angle grain boundaries in nickel
Abstract
Understanding the mechanisms underlying hydrogen embrittlement remains difficult, even in single-element metals. Both microstructure and stress state influence hydrogen distribution in metals and alloys, which impacts deformation and failure. Here, in this work, we use in-situ Kelvin probe force microscopy (KPFM) to monitor the hydrogen distribution in pure nickel over time at 1.1 % and 3.5 % strain. The sample strained to 3.5 % results in preferential hydrogen segregation to high-angle grain boundaries whereas the sample strained to 1.1 % does not exhibit preferential hydrogen segregation. Optical digital image correlation (DIC) shows that hydrogen charging results in both localized and reduced strains during tensile testing of a notched sample. Later stages of deformation and failure (e.g. microcracking) are studied by using in-situ transmission X-ray microscopy (TXM). TXM reveals nanoscale structural changes to a propagating crack in a hydrogen environment. Localized void growth and secondary cracking occur at grain boundaries near the primary crack front. Correlative electron backscattering diffraction (EBSD) is used to relate the cracking at grain boundaries to the hydrogen segregation observed in KPFM. These findings are unified in a proposed hydrogen embrittlement mechanism that describes the interaction of hydrogen with grain boundaries, and the role of grain boundaries in hydrogen embrittlement.
Explore related subjects
Keep this discovery
Explore connections, maps & timelines
Lee, Andrew C. [Stanford University, CA (United States)] (ORCID:0000000271151717), Barsotti, Adam [Stanford University, CA (United States)] (ORCID:000900013636352X), Kang, Jiyun [Stanford University, CA (United States)], Parakh, Abhinav [Stanford University, CA (United States); Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States)] (ORCID:0000000229137073), Paz-Suaznabar, Oscar [Stanford University, CA (United States)] (ORCID:0009000192897729), Sleugh, Andrew [Stanford University, CA (United States)], Lam, Sebastian [University of California, Berkeley, CA (United States)], Newcomb, Christina J. [Stanford University, CA (United States)], Preefer, Molleigh [SLAC National Accelerator Laboratory (SLAC), Menlo Park, CA (United States). Stanford Synchrotron Radiation Lightsource (SSRL)] (ORCID:0000000236998613), Weker, Johanna Nelson [SLAC National Accelerator Laboratory (SLAC), Menlo Park, CA (United States). Stanford Synchrotron Radiation Lightsource (SSRL)], Hosemann, Peter [University of California, Berkeley, CA (United States); Lawrence Berkeley National Laboratory (LBNL), Berkeley, CA (United States)] (ORCID:0000000322812213), Gu, X. Wendy [Stanford University, CA (United States)] (ORCID:0000000154777040). 2025-07-18. Direct observation of strain-enhanced hydrogen segregation and failure at high-angle grain boundaries in nickel. https://doi.org/10.1016/j.actamat.2025.121358
Cite the original work for its findings. Save a collection to share your selection of sources.