Single-Phase Spinel NiCo 2 O 4 as Highly Active and Stable Electrocatalysts for Urea Oxidation Reaction in Urea Electrolysis

Abstract

Exploring and designing a stable and active catalyst for the urea electro-oxidation reaction (UOR, CO(NH 2 ) 2 + 6OH – → CO 2 + N 2 + 5H 2 O + 6e – ) is crucial for the long-term sustainability of ecological systems and clean energy production. We found that spinel NiCo 2 O 4 is a stable and active electrocatalyst for UOR at a relatively low anodic potential without triggering the competing oxygen evolution reaction (OER). A urea electrolysis cell (CO(NH 2 )2 + H 2 O → CO 2 + N 2 + 2H 2 ) utilizing a spinel NiCo 2 O 4 anode and a commercial Pt cathode was further characterized through galvanostatic polarization tests, demonstrating excellent structural stability at various current densities. Post-mortem analysis of long-term urea electrolysis measurements suggested that NiCo 2 O 4 electrocatalysts maintained a stable spinel structure. However, redistribution of Ni 3+ to Ni 2+ valence on the catalyst surface was observed, in contrast to the intact Co valence, indicating that (i) Ni sites are active toward urea adsorption and sequential electro-oxidation; (ii) while urea oxidation proceeds primarily through the direct electro-oxidation mechanism, chemical reactions between the Ni 3+ site and urea occur during long-term electrochemical UOR operation. Density functional theory (DFT) simulations were used to calculate the adsorption energies of urea molecules on NiO, Co 3 O 4 , and NiCo 2 O 4 , revealing the importance of regulating the configuration of adsorbed urea molecules on the NiCo 2 O 4 surface.