High resolution microstructural, chemical studies and localized burnup analysis in an irradiated U–10Zr metallic fuel

Abstract

This study involves high resolution characterization of a sodium bonded solid uranium (U)-10 wt% zirconium (Zr) metallic fuel irradiated in Fast Flux Test Facility (FFTF). The fuel centerline temperature during irradiation was estimated to be around 675 °C with the peak burnup 13.1 atomic percent. Samples for transmission electron microscopy (TEM) and atom probe tomography (APT) were prepared from different regions/zones in the fuel cross section radially to elucidate the microstructural changes and chemical redistribution of solute elements as well as fission products during irradiation experiment. TEM results indicate the irradiation in fast flux testing leads to the formation of extensive Zr-rich precipitates with varying sizes in the U–Zr fuel matrix. APT analysis performed to investigate redistribution of Zr, U and fission products along the radial direction of fuel pin showed Zr-rich precipitates entrapping the fission products in higher concentration as compared to the α-U phases. Here, the local burnup ( 235 U depletion) is found to be consistent, calculated by quantification of 235 U, 236 U and 238 U isotopes from mass spectrum obtained from APT along the radial direction. Zr-rich precipitation and its implication on fuel constitutional redistribution are discussed based on SEM, TEM and APT results.