Three-dimensional nucleation and growth of deformation twins in magnesium

Lee, Sangwon [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000232611813); Pilipchuk, Michael [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0009000198883280); Yildirim, Can [European Synchrotron Radiation Facility (ESRF), Grenoble (France)] (ORCID:0000000249690685); Greeley, Duncan [Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)] (ORCID:000000018946313X); Shi, Qianying [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000184169345); Berman, Tracy D. [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000340275992); Creuziger, Adam [National Inst. of Standards and Technology (NIST), Gaithersburg, MD (United States)] (ORCID:0000000197722066); Rust, Evan [National Inst. of Standards and Technology (NIST), Gaithersburg, MD (United States)]; Detlefs, Carsten [European Synchrotron Radiation Facility (ESRF), Grenoble (France)] (ORCID:0000000325732286); Sundararaghavan, Veera [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000212137958); Allison, John E. [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000163196416); Bucsek, Ashley [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000325607135)

doi:10.1126/science.adv3460

DOE OSTI · 2935370

Three-dimensional nucleation and growth of deformation twins in magnesium

View original source ↗Read source document ↗Export metadata ↓

Abstract

At two-thirds the weight of aluminum, magnesium alloys have the potential to reduce the fuel consumption of transportation vehicles. These advancements depend on our ability to optimize the desirable versus undesirable effects of deformation twins, which are three-dimensional (3D) microstructural domains that form under mechanical stresses. Previously only characterized through surface or thin-film measurements, we here present 3D in situ characterization of deformation twinning inside an embedded grain over mesoscopic fields of view using dark-field x-ray microscopy supported by crystal plasticity finite element analysis. The results revealed the role of triple junctions on twin nucleation and the sequence and irregularity of twin growth and showed that twin-grain junctions, twin-twin junctions, and twin boundaries were the sites of localized dislocation accumulation.

Keep this discovery

BibTeX RIS

Lee, Sangwon [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000232611813), Pilipchuk, Michael [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0009000198883280), Yildirim, Can [European Synchrotron Radiation Facility (ESRF), Grenoble (France)] (ORCID:0000000249690685), Greeley, Duncan [Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)] (ORCID:000000018946313X), Shi, Qianying [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000184169345), Berman, Tracy D. [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000340275992), Creuziger, Adam [National Inst. of Standards and Technology (NIST), Gaithersburg, MD (United States)] (ORCID:0000000197722066), Rust, Evan [National Inst. of Standards and Technology (NIST), Gaithersburg, MD (United States)], Detlefs, Carsten [European Synchrotron Radiation Facility (ESRF), Grenoble (France)] (ORCID:0000000325732286), Sundararaghavan, Veera [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000212137958), Allison, John E. [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000163196416), Bucsek, Ashley [Univ. of Michigan, Ann Arbor, MI (United States)] (ORCID:0000000325607135). 2025-08-07. Three-dimensional nucleation and growth of deformation twins in magnesium. https://doi.org/10.1126/science.adv3460

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related discoveries

NASA NTRS2026

Modeling Study of Hatch Spacing’s Effect on Grain Morphology in Repairing Damaged Metal Parts with Welding and Hatch Spacing’s Potential Use in Lunar Exploration

The welding process is a potential way of repairing a damaged metal component, especially cavity damage caused by a harsh environment like the lunar environment, which is characterized by large temperature differences and reduced gravity. The adjustment of welding parameter (e.g., hatch spacing) can improve production efficiency in the repair process. Seen from the microstructural level, hatch spacing sensitivity affects the metallic grain evolution and morphology in the welding process, which can further influence a repaired part’s mechanical properties; however, the study of hatch spacing’s effect on microstructure is challenging. Traditional experimental procedures are costly and time-consuming, and any change in hatch spacing value needs roll-back of experimental procedure. A modeling study can address the above challenges in experimental observation. In this research, a modeling approach based on the Kinetic Monte Carlo (KMC) Potts theory was used to simulate grain evolution and morphology with three hatch spacings. Through quantifying and analyzing the predicted grain morphologies, the effect of hatch spacing on microstructure in a welding-fabricated part was investigated. The predicted grain morphologies were validated with an EBSD image of welding microstructure, which has been published before. The primary grain morphologies were columnar grains with a small amount of fine equiaxed grains formed in the scanning path centerline. When increasing the hatch spacing, the columnar grains become larger and more lengthy, while the effect of hatch spacing on the equiaxed grains is not obvious.

Welding for repairing↗

NASA NTRS2026

Thermochemical Stability of Ca2Yb8(SiO4)6O2 Apatite in Presence of Molten Calcium-Magnesium-Aluminosilicate (CMAS)

Thermochemical stability of ytterbium silicon oxyapatite Ca 2 Yb 8 (SiO 4 ) 6 O 2 (CYbS) in the presence of molten calcium-magnesium aluminosilicate (CMAS) has been investigated at elevated temperatures for consideration as a thermal and environmental barrier coating (T/EBC) material. CYbS apatite powder was synthesized from the constituent oxides via a solid-state reaction method. Hot-pressed apatite substrates were exposed to molten CMAS at 1200, 1300, and 1400 °C for 1, 10, and 50 h. Development of phases in the interaction region of the heat-treated specimens was monitored using scanning electron microscopy, transmission electron microscopy, high-angle annular dark-field imaging, selected area electron diffraction, and energy dispersive x-ray spectroscopy. Monoclinic cyclosilicate Ca 3 Yb 2 (Si 3 O 9 ) 2 formed from interaction of CYbS apatite with CaO in the CMAS melt at the apatite-CMAS reaction front and continued to nucleate and grow within the residual CMAS in diffusion couples annealed for 1 to 50 h at 1200 °C as well as in those heat treated at 1300 °C for 1 h. Residual CMAS was depleted of Ca when cyclosilicate was present. Dendritic wollastonite (CaSiO3) was observed within the residual CMAS in couples annealed at 1200 and 1300 °C. Ingress of molten CMAS, because of its exponential decrease in viscosity, occurred through open pores and along the grain boundaries of the apatite substrates without any detectable chemical reaction at 1300 and 1400 °C. Results of this study indicate that Ca 2 Yb 8 (SiO 4 ) 6 O 2 apatite has the potential to mitigate the CMAS corrosion up to about 1200 °C but not at higher temperatures.

Narottam P Bansal↗

NASA NTRS2008

Characterization of a New Phase and Its Effect on the Work Characteristics of a Near-Stoichiometric Ni30Pt20Ti50 High-Temperature Shape Memory Alloy (HTSMA)

A new phase observed in a nominal Ni 30 Pt 20 Ti 50 (at.%) high temperature shape memory alloy has been characterized using transmission electron microscopy and 3-D atom probe tomography. This phase forms homogenously in the B2 austenite matrix by a nucleation and growth mechanism and results in a concomitant increase in the martensitic transformation temperature of the base alloy. Although the structure of this phase typically contains a high density of faults making characterization difficult, it appears to be trigonal (-3m point group) with a o ~1.28 nm and c o ~1.4 nm. Precipitation of this phase increases the microhardness of the alloy substantially over that of the solution treated and quenched single-phase material. The effect of precipitation strengthening on the work characteristics of the alloy has been explored through load-biased strain-temperature testing in the solution-treated condition and after aging at 500 ºC for times ranging from 1 to 256 hours. Work output was found to increase in the aged alloy as a result of an increase in transformation strain, but was not very sensitive to aging time. The amount of permanent deformation that occurred during thermal cycling under load was small but increased with increasing aging time and stress. Nevertheless, the dimensional stability of the alloy at short aging times (1-4 hours) was still very good making it a potentially useful material for high-temperature actuator applications.

A Garg↗