Understanding Geometry and Microstructure Interactions In LPBF By Linking Lab Scale Studies To Real Part Case Examples

Abstract

The mechanical properties derived from simple tensile tests are uniquely important in the design and qualification of load bearing metallic components. The tensile properties in standards for wrought metallic materials are generally accessible for design and simulation engineers, but this is not the case for additively manufactured metals. This work investigates the influence of tensile specimen geometry on the mechanical properties of laser powder bed fusion (LPBF) additively manufactured Ti-6Al-4V, particularly in relation to properties measured from specimens excised from an exemplar part. A comprehensive analysis was conducted across various specimen geometries, considering factors such as thermal history, cross-sectional area, shape, and surface roughness. Key findings reveal that sample size, particularly cross-sectional area, significantly affects reported tensile properties, with ASTM E8 flat and round specimens exhibiting differences in elastic modulus (13%), yield strength (17%), ultimate tensile strength (UTS) (14%), and elongation to failure (11%). Additionally, surface roughness was found to have a limited impact on ASTM round geometries, but it becomes critical in thin-walled and small high-throughput samples. The ASTM flat samples closely matched the properties of samples excised from the exemplar part, underscoring the necessity of testing witness samples that accurately represent end-use conditions. Furthermore, mechanical properties of samples built within the stitch zone of the exemplar part demonstrated reduced ductility, highlighting the importance of laser alignment and qualification in multi-laser additive manufacturing processes. Overall, this study emphasizes the need for careful consideration of specimen geometry and testing conditions to ensure accurate reporting of mechanical properties in LPBF Ti-6Al-4V.