Investigation of the irradiation effects in additively manufactured 316L steel resulting in decreased irradiation assisted stress corrosion cracking susceptibility

McMurtrey, Michael D.·Sun, Cheng·Rupp, Ryann E.·Shiau, ChingHeng·Hanbury, R.·Jerred, Nathan D.·O'Brien, Robert C.
View original source ↗Read source document ↗Export metadata ↓

Abstract

While additive manufacturing (AM) is an area of increasing interest to the nuclear industry, there are significant research and development needs prior to successful implementation of additively manufactured components into reactors. AM steel behaves differently than traditional wrought material, as has been observed in numerous mechanical testing studies. The nuclear industry must also understand the material response to irradiation. This work examines the irradiation damage and the irradiation assisted stress corrosion cracking behavior (IASCC) of both proton irradiated AM and wrought 316L steel. For IASCC testing, specimens were strained to 4% plastic strain in a simulated boiling water reactor environment (288°C, 0.2 µS/cm). Transmission and scanning electron microscopy, confocal microscopy, and X-ray computed tomography were used to examine coupons of the material as well as tensile bars used in the IASCC testing. This work found that the wrought 316L was more susceptible to IASCC than the AM steel, however, some IASCC was observed in the AM steel when tested with the tensile axis parallel to the build direction. Electron microscopy has shown significantly fewer radiation induced voids formed in the AM steel. While the pre-existing pore network in the AM steel may act as a sink to point defects, this is not expected to be the major factor in the reduced swelling observed in the AM steel. The lower density of radiation induced voids was expected to contribute to the IASCC resistance by decreasing the localization of deformation in the irradiated specimens, however, severity of localized deformation in AM steel, measured in dislocation channel spacing and height, was similar or more severe to that found in wrought. In conclusion, the presence of severe cracking in the wrought specimens did not allow for a direct comparison of localized deformation severities between the AM and wrought steel.

Explore related subjects

Additive manufacturingIASCCIrradiation effects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

McMurtrey, Michael D., Sun, Cheng, Rupp, Ryann E., Shiau, ChingHeng, Hanbury, R., Jerred, Nathan D., O'Brien, Robert C.. 2020-12-17. Investigation of the irradiation effects in additively manufactured 316L steel resulting in decreased irradiation assisted stress corrosion cracking susceptibility. https://doi.org/10.1016/j.jnucmat.2020.152739

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Predicting roughness effects in additively manufactured coolant channels with helical enhancements

Additive manufacturing (AM) is a promising technique for fabrication of complex geometries such as those expected to be utilized in the blanket, first wall, and divertor. In the case of cooling, metallic AM may be exploited to embed geometric enhancements (ribs, rifling, etc.) to improve cooling performance. However, due to the roughness of these unfinished internal AM surfaces, prediction of thermal hydraulic performance in such channels is difficult. In this work, we consider a methodology for predicting pressure drop and heat transfer in AM channels containing helical enhancements (e.g. helical ribs, twisted tapes) that allows the incorporation of roughness data through conventional pipe flow correlations. This methodology is tested using experimental friction factor and heat transfer coefficient data from high-pressure helium coolant flow measurements in AM stainless steel tubes fabricated by laser powder bed fusion. Both a featureless AM tube and one containing helical ribs were considered alongside a conventionally manufactured smooth tube. The AM surface roughness is obtained by profilometry and used to predict an equivalent sand-grain roughness, with this equivalent roughness confirmed through AM featureless tube measurements. Under the proposed methodology, this roughness information is incorporated into predictions of friction factor and Nusselt number for the rifled tube. Furthermore, these predictions agree well with experimental data across a large range of Reynolds numbers, encouraging the use of this methodology for thermal hydraulic analysis of similar systems and design of future coolant channel geometries.

Additive manufacturing↗
DOE OSTI2026

High-throughput oxidation screening and down-selection of refractory high entropy alloys in the Al-Cr-Mo-Nb-Ta-Ti system

Rapid experimentation and characterization are ever-present needs in the discovery of high entropy alloys. High entropy alloy systems are difficult to survey with systematic composition sweeps using traditional synthesis methods. The number of distinct compositions in even a four-element system is experimentally intractable. Exploration of these, and higher-element systems, necessitates thermodynamic prediction coupled with an automated sample creation method and a rapid screening methodology to effectively down-select alloys with targeted properties. As a result, a high-throughput method for evaluating the oxidation performance of refractory high entropy alloys was developed and tested. The six-element system of aluminum, chromium, molybdenum, niobium, tantalum, and titanium was evaluated for single phase stability and short-duration oxidation resistance. Target compositions were initially determined via thermodynamic predictions of single-phase stability across a wide temperature range. A twenty-five-sample build plate was produced using directed energy deposition additive manufacturing. After fabrication, the twenty-five 1 cm 3 samples were heat treated and characterized for composition and phase identification. The build plate was exposed to a high temperature oxidizing environment at 1000 °C for three hours. After oxidation, the composition, morphology, and chemistry of the oxides formed were characterized. Of the twenty-five samples produced, nine exhibited a favorable oxidation response, from which a single-phase BCC alloy at a composition of Al 13 Cr 7 Mo 19 Nb 18 Ta 26 Ti 17 was identified as the alloy with the most protective oxidation coating with a thin, adherent oxide scale. Finally, the complete experimental down-selection—from machine setup to final alloy identification—required approximately 45 labor hours, demonstrating a rapid validation for alloy discovery.

Additive manufacturing↗
DOE OSTI2026

Background-Oriented Schlieren Velocimetry of Helium Coolant Flow in Additively Manufactured Channels

High-pressure helium gas cooling is an attractive solution for thermal management of the fusion blanket first wall, as this coolant is chemically and neutronically inert and separable from hydrogenic species. However, due to the low thermal mass of helium, geometric optimization of these channels is required to provide sufficient cooling at manageable flow rates and pumping burdens. Increasingly, analysis and optimization of these coolant channels rely on computational fluid dynamics (CFD) simulations, and these require relevant experimental data for turbulence model validation. Toward this end, a high-pressure helium gas flow visualization system has been employed to image the flow of helium in flow channels with one-sided heating, mimicking the blanket first wall environment. Flow of helium at 4 MPa pressure and flow rates up to 68 g/s (Reynolds number 57 000) is supplied to rectangular channel test sections, with uniform heating applied to the bottom wall of the channel at heat fluxes varied between roughly 50 and 130 kW/m2. A high-speed camera is used to image index of refraction (IOR) gradients in the fluid via background-oriented schlieren (BOS), and temperature and pressure instrumentation are used to characterize thermal-hydraulic performance of each channel. Cross correlation of time-resolved BOS images is then used to calculate time-averaged 2-D helium velocity fields. Flow in additively manufactured (AM) channels is examined in this manner, including both featureless channels and those containing baffling as a heat transfer enhancement. The flow distribution seen in the featureless case differs significantly from that seen in prior simulations, whereas the flow in the baffled case shows the predicted behavior of flow forced along the heated wall. This augmented flow distribution is seen to increase the heat transfer coefficient in the baffled test section. Here, strategies are discussed for ongoing and future validation of these simulations, with the aim of model deployment for blanket cooling design and optimization.

Additive manufacturing↗