Advanced Materials & Manufacturing Technology (AMMT): Process understanding for qualifying LPBF 316H SS

Abstract

Investigations were conducted in fiscal years (FY) 2023 and 2024 to gather relevant data sets addressing challenges related to qualifying 316H stainless steel (SS) for use in future nuclear reactors. This work was a collaborative effort involving researchers from Idaho National Laboratory (INL), Argonne National Laboratory (ANL), and Oak Ridge National Laboratory (ORNL). Key outcomes included: • Development of process-structure-property data sets to better understand the relationships between manufacturing processes, material structure, and performance characteristics. • Establishment of an in-situ monitoring system to link these various data sets together. • Detailed characterization of the raw material feedstock to further strengthen the understanding of process-structure and process-property relationships. Building on this foundation, in FY25 there was interest in exploring the behavior of additively manufactured 316H SS under different test conditions to support the overall material qualification process. Los Alamos National Laboratory (LANL) was tasked with providing specimen samples to the collaborating labs, who then conducted a round-robin study examining factors like selective heat treatment, low-cycle fatigue (LCF), and tensile-creep (T-C) properties. Additionally, high-temperature differential scanning calorimetry (DSC) was performed by LANL to better understand how the material's thermal characteristics change as it is heated up to the melting point. This provided a more comprehensive understanding of the material's behavior. The combined results from these investigations could potentially be used to support the inclusion of 316H stainless steel in Section III, Division 5 of the relevant codes and standards, allowing its use in future nuclear reactor applications.